Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 440FSe (ASTM A959:2011) and IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 440FSe is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X07Cr17 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1). ASTM A959 440FSe is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 440FSe vs IS 11169 (Part 2) X07Cr17 is a 88.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 440FSe:
IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
88.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 440FSe IS 11169 (Part 2) X07Cr17
Standard ASTM A959:2011 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 <=0.12
Cr (%) 16.0-18.0 16.0-18.0
Mn (%) <=1.25 <=1.0
P (%) <=0.06 <=0.045
S (%) <=0.06 <=0.030
Se (%) >=0.15 Not specified
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 440FSe IS 11169 (Part 2) X07Cr17
Yield Strength (0.2% proof) Not specified >=270 MPa
Tensile Strength Not specified 450-600 MPa
Elongation Not specified >=20%
Condition Not specified Annealed reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 440FSe
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Key Differences
Can ASTM A959 440FSe Be Substituted With IS 11169 (Part 2) X07Cr17?
ASTM A959 440FSe and IS 11169 (Part 2) X07Cr17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 440FSe
0 active listings and RFQs →
IS 11169 (Part 2) X07Cr17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 440FSe and IS 11169 (Part 2) X07Cr17?
ASTM A959 440FSe specifies Se which is not specified for IS 11169 (Part 2) X07Cr17.
Can ASTM A959 440FSe be substituted with IS 11169 (Part 2) X07Cr17?
ASTM A959 440FSe and IS 11169 (Part 2) X07Cr17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.