ASTM A959 442 vs IS 1570 (Part 5) X07Cr17

Strong Match — 86.3% match based on chemical composition and mechanical property overlap.

ASTM A959 442 (ASTM A959:2011) and IS 1570 (Part 5) X07Cr17 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 442 is defined under ASTM International, originating from United States, while IS 1570 (Part 5) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 442 vs IS 1570 (Part 5) X07Cr17 is a 86.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.3%.

Frequently Compared With ASTM A959 442:
IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
86.3%
MECHANICAL MATCH
No shared data
OVERALL
86.3%
Specifications
Property ASTM A959 442 IS 1570 (Part 5) X07Cr17
Standard ASTM A959:2011 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.20 <=0.12
Cr (%) 18.0-23.0 16.0-18.0
Mn (%) <=1.00 <=1.0
Ni (%) <=0.60 <=0.5
P (%) <=0.040 <=0.040
S (%) <=0.040 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 442 IS 1570 (Part 5) X07Cr17
Tensile Strength Not specified >=450 MPa
Yield Strength Not specified >=205 MPa (0.2 % proof stress)
Elongation Not specified >=22.0% (50 mm)
Hardness Not specified <=183 HB; <=88 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
ASTM A959 442
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 1570 (Part 5) X07Cr17
Not documented
Can ASTM A959 442 Be Substituted With IS 1570 (Part 5) X07Cr17?
ASTM A959 442 and IS 1570 (Part 5) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X07Cr17 is often considered as a substitute for ASTM A959 442 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 442
0 active listings and RFQs →
IS 1570 (Part 5) X07Cr17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 442 and IS 1570 (Part 5) X07Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 442 be substituted with IS 1570 (Part 5) X07Cr17?
ASTM A959 442 and IS 1570 (Part 5) X07Cr17 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X07Cr17 is often considered as a substitute for ASTM A959 442 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.