IS 1570 (Part 5):1985 X07Cr17 Steel: Specifications & Listings

IS 1570 (Part 5):1985 X07Cr17: X07Cr17: high alloy, stainless or heat-resisting steel. Specified in IS 1570 (Part 5):1985.

Category: Stainless Steel
Grade Details
GradeIS 1570 (Part 5):1985 X07Cr17
Standard IS 1570 (Part 5):1985
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 6911 X07Cr17 IS 6911:1992 India No activity yet
ASTM A959 430Ti ASTM A959:2011 USA No activity yet
ASTM A959 442 ASTM A959:2011 USA No activity yet
ASTM A959 443 ASTM A959:2011 USA No activity yet
BS 970 (Part 1) 430S17 BS 970 (Part 1):1991 UK No activity yet
ASTM A240/A240M S43000 ASTM A240/A240M:2025 USA No activity yet
IS 5522 X07Cr17 IS 5522:2014 India No activity yet
JIS G4304 SUS429 JIS G4304:2021 Japan No activity yet
JIS G4304 SUS430 JIS G4304:2021 Japan No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
BS 970 EN60 BS 970:1955 Strong Match
ASTM A240/A240M S43000 ASTM A240/A240M:2025 Strong Match
BS 970 (Part 1) 430S17 BS 970 (Part 1):1991 Strong Match
BS 970 (Part 3) 430S17 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 430S17 BS 970 (Part 1):1983 Strong Match
JIS G4304 SUS429 JIS G4304:2021 Strong Match
JIS G4305 SUS429 JIS G4305:2012 Strong Match
ASTM A959 430Ti ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Ni
<=0.12 <=1.0 <=1.0 <=0.040 <=0.030 16.0-18.0 <=0.5
Mechanical Properties
Tensile Strength >=450 MPa
Yield Strength >=205 MPa (0.2 % proof stress)
Elongation >=22.0% (50 mm)
Hardness <=183 HB; <=88 HRB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2)

More data from IS 1570 (Part 5):1985

From the standard
Annealed, quenched or solution treated plates, sheets and strips 5 properties
Tensile strength, min
450 MPa
0.2 % proof stress, min
205 MPa
Elongation in 50 mm, min
22.0%
Brinell hardness, max
183 HB
Rockwell B hardness, max
88 HRB
Source: IS 1570 (Part 5):1985, Table 2
Annealed, quenched or solution treated bars and flats 4 properties
Tensile strength, min
483 MPa
0.2 % proof stress, min
276 MPa
Elongation in 50 mm, min
20%
Reduction of area, min
45%
Source: IS 1570 (Part 5):1985, Table 3
Recommended heat treatment 2 entries
Annealing temperature
750 to 850 deg C
Annealing cooling medium
air, water
A annealing, S softening, ST solution treatment, Q quenching, T tempering, P patenting.
Source: IS 1570 (Part 5):1985, Table 7

Active IS 1570 (Part 5):1985 X07Cr17 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 1570 (Part 5):1985 X07Cr17 listings at this time.

Register for Alerts

Buyer RFQs for IS 1570 (Part 5):1985 X07Cr17

+ Post an RFQ for this grade

No open buyer requirements for IS 1570 (Part 5):1985 X07Cr17 at this time.

Register for Alerts