Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 800H (ASTM A959:2011) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 800H is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 800H is defined under ASTM International, originating from United States, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 800H vs ASTM A959 .- is a 61.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 800H:
IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
61.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 800H ASTM A959 .-
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
Al (%) 0.15-0.60 Not specified
C (%) 0.05-0.10 <=0.030
Cr (%) 19.0-23.0 18.0-20.0
Cu (%) <=0.75 Not specified
Fe (%) >=39.5 Not specified
Mn (%) <=1.50 <=1.00
Ni (%) 30.0-35.0 <=0.50
P (%) <=0.045 <=0.040
S (%) <=0.015 <=0.030
Si (%) <=1.00 <=1.00
Ti (%) 0.15-0.60 0.07-0.30
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 800H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A959 800H Be Substituted With ASTM A959 .-?
ASTM A959 800H and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 800H
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 800H and ASTM A959 .-?
ASTM A959 800H specifies Al, Cu, Fe which are not specified for ASTM A959 .-. ASTM A959 .- specifies Cb, N which are not specified for ASTM A959 800H.
Can ASTM A959 800H be substituted with ASTM A959 .-?
ASTM A959 800H and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.