Post Stock Login Register

ASTM A959 N08020 vs ASTM A959 S35125

Close Alternative — 75.2% match based on chemical composition and mechanical property overlap.

ASTM A959 N08020 (ASTM A959:2011) and ASTM A959 S35125 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 N08020 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 S35125 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 N08020 is defined under ASTM International, originating from United States, while ASTM A959 S35125 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 N08020 vs ASTM A959 S35125 is a 75.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 75.2%.

Frequently Compared With ASTM A959 N08020:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
75.2%
MECHANICAL MATCH
No shared data
OVERALL
75.2%
Specifications
Property ASTM A959 N08020 ASTM A959 S35125
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.07 <=0.10
Cr (%) 19.0-21.0 20.0-23.0
Cu (%) 3.0-4.0 Not specified
Mn (%) <=2.00 1.00-1.50
Mo (%) 2.00-3.00 2.00-3.00
Ni (%) 32.0-38.0 31.0-35.0
P (%) <=0.045 <=0.045
S (%) <=0.035 <=0.015
Si (%) <=1.00 <=0.50
Cb (%) Not specified 0.25-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 N08020
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 S35125
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A959 N08020 Be Substituted With ASTM A959 S35125?
ASTM A959 N08020 and ASTM A959 S35125 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 N08020
0 active listings and RFQs →
ASTM A959 S35125
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 N08020 and ASTM A959 S35125?
ASTM A959 N08020 specifies Cu which is not specified for ASTM A959 S35125. ASTM A959 S35125 specifies Cb which is not specified for ASTM A959 N08020.
Can ASTM A959 N08020 be substituted with ASTM A959 S35125?
ASTM A959 N08020 and ASTM A959 S35125 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.