Close Alternative — 82.8% match based on chemical composition and mechanical property overlap.

ASTM A959 N08700 (ASTM A959:2011) and ASTM A959 904L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 N08700 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 904L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 N08700 is defined under ASTM International, originating from United States, while ASTM A959 904L is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 N08700 vs ASTM A959 904L is a 82.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.8%.

Frequently Compared With ASTM A959 N08700:
GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
82.8%
MECHANICAL MATCH
No shared data
OVERALL
82.8%
Specifications
Property ASTM A959 N08700 ASTM A959 904L
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.020
Cr (%) 19.0-23.0 19.0-23.0
Cu (%) <=0.50 1.00-2.00
Mn (%) <=2.00 <=2.00
Mo (%) 4.3-5.0 4.0-5.0
Ni (%) 24.0-26.0 23.0-28.0
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 N08700
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 904L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A959 N08700 Be Substituted With ASTM A959 904L?
ASTM A959 N08700 and ASTM A959 904L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 N08700
0 active listings and RFQs →
ASTM A959 904L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 N08700 and ASTM A959 904L?
ASTM A959 904L specifies N which is not specified for ASTM A959 N08700.
Can ASTM A959 N08700 be substituted with ASTM A959 904L?
ASTM A959 N08700 and ASTM A959 904L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.