ASTM A959 S30430 vs IS 11169 (Part 2) X02Cr19Ni9

Strong Match — 91.1% match based on chemical composition and mechanical property overlap.

ASTM A959 S30430 (ASTM A959:2011) and IS 11169 (Part 2) X02Cr19Ni9 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S30430 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X02Cr19Ni9 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11). ASTM A959 S30430 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X02Cr19Ni9 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S30430 vs IS 11169 (Part 2) X02Cr19Ni9 is a 91.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.1%.

Frequently Compared With ASTM A959 S30430:
GOST 5632 08X18H10 EN 10088-1 1.4301 ASTM A959 .- IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
91.1%
MECHANICAL MATCH
No shared data
OVERALL
91.1%
Specifications
Property ASTM A959 S30430 IS 11169 (Part 2) X02Cr19Ni9
Standard ASTM A959:2011 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.03 <=0.030
Cr (%) 17.0-19.0 17.5-19.5
Cu (%) 3.0-4.0 <=1.00
Mn (%) <=2.00 <=2.00
Ni (%) 8.0-10.0 8.0-10.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S30430 IS 11169 (Part 2) X02Cr19Ni9
Reduction of Area, solution annealed (+AT) Not specified >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=630 MPa (over 5 to 50 mm)
Typical Applications
ASTM A959 S30430
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X02Cr19Ni9
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Key Differences
Can ASTM A959 S30430 Be Substituted With IS 11169 (Part 2) X02Cr19Ni9?
ASTM A959 S30430 and IS 11169 (Part 2) X02Cr19Ni9 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr19Ni9 is often considered as a substitute for ASTM A959 S30430 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S30430
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr19Ni9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S30430 and IS 11169 (Part 2) X02Cr19Ni9?
IS 11169 (Part 2) X02Cr19Ni9 specifies N which is not specified for ASTM A959 S30430.
Can ASTM A959 S30430 be substituted with IS 11169 (Part 2) X02Cr19Ni9?
ASTM A959 S30430 and IS 11169 (Part 2) X02Cr19Ni9 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr19Ni9 is often considered as a substitute for ASTM A959 S30430 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.