ASTM A959 S31803 vs IS 11169 (Part 2) X02Cr22Ni5Mo3N

Strong Match — 98% match based on chemical composition and mechanical property overlap.

ASTM A959 S31803 (ASTM A959:2011) and IS 11169 (Part 2) X02Cr22Ni5Mo3N (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S31803 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X02Cr22Ni5Mo3N is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 2 to 25 mm (clause 1.1, table 12). ASTM A959 S31803 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X02Cr22Ni5Mo3N is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S31803 vs IS 11169 (Part 2) X02Cr22Ni5Mo3N is a 98% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98%.

Frequently Compared With ASTM A959 S31803:
ASTM A959 2205 ASTM A959 2304 ASTM A959 255 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
98%
MECHANICAL MATCH
No shared data
OVERALL
98%
Specifications
Property ASTM A959 S31803 IS 11169 (Part 2) X02Cr22Ni5Mo3N
Standard ASTM A959:2011 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 21.0-23.0 21.0-23.0
Mn (%) <=2.00 <=2.00
Mo (%) 2.5-3.5 2.50-3.50
N (%) 0.08-0.20 0.10-0.2
Ni (%) 4.5-6.5 4.5-6.5
P (%) <=0.030 <=0.035
S (%) <=0.020 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S31803 IS 11169 (Part 2) X02Cr22Ni5Mo3N
Reduction of Area, solution annealed (+AT) Not specified >=55% (over 2 to 25 mm)
Tensile Strength, solution annealed (+AT) Not specified <=880 MPa (over 2 to 25 mm)
Typical Applications
ASTM A959 S31803
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X02Cr22Ni5Mo3N
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 2 to 25 mm (clause 1.1, Table 12)
Can ASTM A959 S31803 Be Substituted With IS 11169 (Part 2) X02Cr22Ni5Mo3N?
ASTM A959 S31803 and IS 11169 (Part 2) X02Cr22Ni5Mo3N overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr22Ni5Mo3N is often considered as a substitute for ASTM A959 S31803 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S31803
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr22Ni5Mo3N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S31803 and IS 11169 (Part 2) X02Cr22Ni5Mo3N?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S31803 be substituted with IS 11169 (Part 2) X02Cr22Ni5Mo3N?
ASTM A959 S31803 and IS 11169 (Part 2) X02Cr22Ni5Mo3N overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr22Ni5Mo3N is often considered as a substitute for ASTM A959 S31803 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.