IS 11169 (Part 2):2023 X02Cr22Ni5Mo3N Steel: Specifications & Listings
IS 11169 (Part 2):2023 X02Cr22Ni5Mo3N: Cold heading quality austenitic-ferritic stainless steel X02Cr22Ni5Mo3N to IS 11169 (Part 2):2023, supplied as wire rod, bars or wire of 2 to 25 mm. Maximum tensile strength solution annealed is 880 MPa.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Cr
Mn
Mo
N
Ni
P
S
Si
<=0.030
21.0-23.0
<=2.00
2.50-3.50
0.10-0.2
4.5-6.5
<=0.035
<=0.015
<=1.00
Mechanical Properties
Reduction of Area, solution annealed (+AT)
>=55% (over 2 to 25 mm)
Tensile Strength, solution annealed (+AT)
<=880 MPa (over 2 to 25 mm)
More data from IS 11169 (Part 2):2023
From the standard
Other composition limitsfrom the table notes
Values
Maximum unless a range is given (ladle analysis)
Steel type
Austenitic-ferritic
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 2):2023, Table 10 and its notes
Tensile strength and reduction of area by delivery conditionby delivery condition and size
Delivery condition
Diameter (mm)
Tensile strength, max (MPa)
Reduction of area, min (%)
+AT or +AT+PE
over 2 to 5
880
55
+AT or +AT+PE
over 5 to 10
880
55
+AT or +AT+PE
over 10 to 25
880
55
+AT+C
over 5 to 10
1020
-
+AT+C
over 10 to 25
1000
-
+AT+C+AT
over 2 to 5
950
55
+AT+C+AT
over 5 to 10
900
55
+AT+C+AT
over 10 to 25
880
55
+AT+C+AT+LC
over 2 to 5
1010
50
+AT+C+AT+LC
over 5 to 10
970
50
Codes: +AT solution annealed, +A soft annealed, +PE peeled, +C cold drawn, +LC skin passed. Diameter ranges are over the first figure up to and including the second. No reduction of area is specified for +AT+C. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 2):2023, Table 12