ASTM A959 S32001 vs ASTM A240/A240M S32001

Strong Match — 100% match based on chemical composition and mechanical property overlap.

ASTM A959 S32001 (ASTM A959:2011) and ASTM A240/A240M S32001 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32001 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S32001 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 S32001 is defined under ASTM International, originating from United States, while ASTM A240/A240M S32001 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S32001 vs ASTM A240/A240M S32001 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With ASTM A959 S32001:
ASTM A959 2304 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH ASTM A959 26-3-3
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property ASTM A959 S32001 ASTM A240/A240M S32001
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 19.5-21.5 19.5-21.5
Cu (%) <=1.00 <=1.00
Mn (%) 4.0-6.0 4.00-6.00
Mo (%) <=0.60 <=0.60
N (%) 0.05-0.17 0.05-0.17
Ni (%) 1.00-3.00 1.00-3.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32001 ASTM A240/A240M S32001
Tensile Strength Not specified >=620 MPa
Yield Strength Not specified >=450 MPa
Elongation Not specified >=25%
Hardness Not specified <=25 HRC
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 S32001
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S32001
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 S32001 Be Substituted With ASTM A240/A240M S32001?
ASTM A959 S32001 and ASTM A240/A240M S32001 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S32001 is often considered as a substitute for ASTM A959 S32001 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S32001
0 active listings and RFQs →
ASTM A240/A240M S32001
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32001 and ASTM A240/A240M S32001?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S32001 be substituted with ASTM A240/A240M S32001?
ASTM A959 S32001 and ASTM A240/A240M S32001 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S32001 is often considered as a substitute for ASTM A959 S32001 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.