ASTM A959 S32654 vs IS 6603 X01Cr25Ni22Mo2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

ASTM A959 S32654 (ASTM A959:2011) and IS 6603 X01Cr25Ni22Mo2 (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32654 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6603 X01Cr25Ni22Mo2 is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars. ASTM A959 S32654 is defined under ASTM International, originating from United States, while IS 6603 X01Cr25Ni22Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S32654 vs IS 6603 X01Cr25Ni22Mo2 is a 70.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With ASTM A959 S32654:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
70.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property ASTM A959 S32654 IS 6603 X01Cr25Ni22Mo2
Standard ASTM A959:2011 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Cr (%) 24.0-25.0 24.0-26.0
Cu (%) 0.30-0.60 Not specified
Mn (%) 2.0-4.0 <=2.00
Mo (%) 7.0-8.0 2.00-2.50
N (%) 0.45-0.55 0.10-0.16
Ni (%) 21.0-23.0 21.0-23.0
P (%) <=0.030 <=0.025
S (%) <=0.005 <=0.010
Si (%) <=0.50 <=0.70
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32654 IS 6603 X01Cr25Ni22Mo2
Tensile Strength Not specified 540-740 MPa
Yield Strength Not specified >=250 MPa
Elongation Not specified >=35%
Condition Not specified Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
ASTM A959 S32654
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6603 X01Cr25Ni22Mo2
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can ASTM A959 S32654 Be Substituted With IS 6603 X01Cr25Ni22Mo2?
ASTM A959 S32654 and IS 6603 X01Cr25Ni22Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
ASTM A959 S32654
0 active listings and RFQs →
IS 6603 X01Cr25Ni22Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32654 and IS 6603 X01Cr25Ni22Mo2?
ASTM A959 S32654 specifies Cu which is not specified for IS 6603 X01Cr25Ni22Mo2.
Can ASTM A959 S32654 be substituted with IS 6603 X01Cr25Ni22Mo2?
ASTM A959 S32654 and IS 6603 X01Cr25Ni22Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.