ASTM A959 S32906 vs EN 10088-1 1.4845

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 S32906 (ASTM A959:2011) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S32906 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. ASTM A959 S32906 is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 S32906 vs EN 10088-1 1.4845 is a 50.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 S32906:
ASTM A959 29-4 ASTM A959 29-4-2 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 29-4C ASTM A959 2507
Match Breakdown
CHEMISTRY MATCH
50.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 S32906 EN 10088-1 1.4845
Standard ASTM A959:2011 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.10
Cr (%) 28.0-30.0 24.0–26.0
Cu (%) <=0.80 Not specified
Mn (%) 0.80-1.50 ≤2.00
Mo (%) 1.50-2.60 Not specified
N (%) 0.30-0.40 Not specified
Ni (%) 5.8-7.5 19.0–22.0
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Si (%) <=0.50 ≤1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S32906 EN 10088-1 1.4845
Tensile Strength Not specified ≥515 MPa
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Max Service Temp Not specified 1100°C continuous
Typical Applications
ASTM A959 S32906
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can ASTM A959 S32906 Be Substituted With EN 10088-1 1.4845?
ASTM A959 S32906 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 S32906
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
ASTM A959 S32906
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S32906 and EN 10088-1 1.4845?
ASTM A959 S32906 specifies Cu, Mo, N, P which are not specified for EN 10088-1 1.4845.
Can ASTM A959 S32906 be substituted with EN 10088-1 1.4845?
ASTM A959 S32906 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.