ASTM A959 S34751 vs IS 11169 (Part 2) X02Cr19Ni10

Close Alternative — 82.6% match based on chemical composition and mechanical property overlap.

ASTM A959 S34751 (ASTM A959:2011) and IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S34751 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X02Cr19Ni10 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1). ASTM A959 S34751 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S34751 vs IS 11169 (Part 2) X02Cr19Ni10 is a 82.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.6%.

Frequently Compared With ASTM A959 S34751:
EN 10088-1 1.4401 GOST 5632 06Kh23N28 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
82.6%
MECHANICAL MATCH
No shared data
OVERALL
82.6%
Specifications
Property ASTM A959 S34751 IS 11169 (Part 2) X02Cr19Ni10
Standard ASTM A959:2011 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) <=0.015 <=0.030
Cb (%) 0.20-0.50 Not specified
Cr (%) 17.0-20.0 17.5-20.0
Mn (%) <=2.00 <=2.0
N (%) 0.06-0.10 Not specified
Ni (%) 9.0-13.0 8.0-12.0
P (%) <=0.020 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=0.75 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S34751 IS 11169 (Part 2) X02Cr19Ni10
Yield Strength (0.2% proof) Not specified >=175 MPa
Tensile Strength Not specified 450-700 MPa
Elongation Not specified >=50%
Impact (U-notch 5 mm) Not specified >=60 J
Condition Not specified Quenched reference test piece (Table 6 treatment)
Typical Applications
ASTM A959 S34751
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Key Differences
Can ASTM A959 S34751 Be Substituted With IS 11169 (Part 2) X02Cr19Ni10?
ASTM A959 S34751 and IS 11169 (Part 2) X02Cr19Ni10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S34751
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr19Ni10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S34751 and IS 11169 (Part 2) X02Cr19Ni10?
ASTM A959 S34751 specifies Cb, N which are not specified for IS 11169 (Part 2) X02Cr19Ni10.
Can ASTM A959 S34751 be substituted with IS 11169 (Part 2) X02Cr19Ni10?
ASTM A959 S34751 and IS 11169 (Part 2) X02Cr19Ni10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.