IS 11169 (Part 2):1989 X02Cr19Ni10: Cold heading quality austenitic stainless steel X02Cr19Ni10 to IS 11169 (Part 2):1989, supplied as wire, wire rod or bars and ordered on chemical composition alone or with mechanical properties. The standard was reaffirmed in 2004.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):1989 X02Cr19Ni10
Standard IS 11169 (Part 2):1989
ApplicationsCold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 6911 X02Cr19Ni10 IS 6911:1992 India No activity yet
ASTM A959 304L ASTM A959:2011 USA No activity yet
ASTM A959 304LN ASTM A959:2011 USA No activity yet
ASTM A959 304LHN ASTM A959:2011 USA No activity yet
BS 970 (Part 3) 304S11 BS 970 (Part 3):1991 UK No activity yet
EN 10088-1 X2CrNi18-9 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrNiN18-10 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 304L ASTM A959:2011 Strong Match
BS 970 (Part 3) 304S11 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 304S11 BS 970 (Part 1):1983 Strong Match
EN 10088-1 X2CrNi18-9 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNi18-9 EN 10088-1:2023 Strong Match
ASTM A959 304LN ASTM A959:2011 Strong Match
ASTM A959 304LHN ASTM A959:2011 Strong Match
EN 10088-1 X2CrNi19-11 EN 10088-1:2014 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn Ni Cr S P
<=0.030 <=1.0 <=2.0 8.0-12.0 17.5-20.0 <=0.030 <=0.045
Mechanical Properties
Yield Strength (0.2% proof) >=175 MPa
Tensile Strength 450-700 MPa
Elongation >=50%
Impact (U-notch 5 mm) >=60 J
Condition Quenched reference test piece (Table 6 treatment)

More data from IS 11169 (Part 2):1989

From the standard
Properties in the delivery condition 3 conditions
Delivery conditionTensile strength, max (MPa)Reduction of area, min (%)
Quenched (Q), or quenched and peeled (Q+P)63055
Cold drawn and quenched (C+Q)63055
Cold drawn, quenched and lightly cold reduced (C+Q+LC)68055
Lightly cold reduced means, for example, a reduction of 5 percent. Table 4 prints the third condition as E+Q+LC; clause 10.2 gives C+Q+LC.
Source: IS 11169 (Part 2):1989, Table 4, clauses 8.1 and 10
Heat treatment of reference test pieces 1 value
Quenching temperature
1000 to 1050 °C
Treatment for the test pieces on which the mechanical properties are checked when ordered to requirement class 2 (clause 8.2).
Source: IS 11169 (Part 2):1989, Table 6

Active IS 11169 (Part 2):1989 X02Cr19Ni10 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):1989 X02Cr19Ni10 listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):1989 X02Cr19Ni10

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):1989 X02Cr19Ni10 at this time.

Register for Alerts