ASTM A959 S40976 vs ASTM A240/A240M S40975

Strong Match — 88.9% match based on chemical composition and mechanical property overlap.

ASTM A959 S40976 (ASTM A959:2011) and ASTM A240/A240M S40975 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S40976 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A240/A240M S40975 is commonly used for pressure vessels and general applications (plate, sheet and strip). ASTM A959 S40976 is defined under ASTM International, originating from United States, while ASTM A240/A240M S40975 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S40976 vs ASTM A240/A240M S40975 is a 88.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 88.9%.

Frequently Compared With ASTM A959 S40976:
EN 10088-1 1.4301 GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
88.9%
MECHANICAL MATCH
No shared data
OVERALL
88.9%
Specifications
Property ASTM A959 S40976 ASTM A240/A240M S40975
Standard ASTM A959:2011 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 10.5-11.7 10.5-11.7
Mn (%) <=1.00 <=1.00
N (%) <=0.040 <=0.030
Ni (%) 0.75-1.00 0.50-1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Ti (%) >=0.05 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S40976 ASTM A240/A240M S40975
Tensile Strength Not specified >=415 MPa
Yield Strength Not specified >=275 MPa
Elongation Not specified >=20%
Hardness Not specified <=197 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
ASTM A959 S40976
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A240/A240M S40975
Pressure vessels and general applications (plate, sheet and strip)
Can ASTM A959 S40976 Be Substituted With ASTM A240/A240M S40975?
ASTM A959 S40976 and ASTM A240/A240M S40975 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S40975 is often considered as a substitute for ASTM A959 S40976 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S40976
0 active listings and RFQs →
ASTM A240/A240M S40975
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S40976 and ASTM A240/A240M S40975?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S40976 be substituted with ASTM A240/A240M S40975?
ASTM A959 S40976 and ASTM A240/A240M S40975 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S40975 is often considered as a substitute for ASTM A959 S40976 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.