Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A959 S41603 (ASTM A959:2011) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S41603 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. ASTM A959 S41603 is defined under ASTM International (United States).

As per chemical composition, ASTM A959 S41603 vs GOST 5632 06Kh23N28 is a 66.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A959 S41603:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
66.4%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property ASTM A959 S41603 GOST 5632 06Kh23N28
Standard ASTM A959:2011 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 ≤0.06
Cr (%) 12.0-14.0 22.0–25.0
Mn (%) <=1.25 ≤2.00
P (%) <=0.06 Not specified
S (%) >=0.15 Not specified
Si (%) <=1.00 ≤0.80
Ni (%) Not specified 26.0–29.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S41603 GOST 5632 06Kh23N28
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
ASTM A959 S41603
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can ASTM A959 S41603 Be Substituted With GOST 5632 06Kh23N28?
ASTM A959 S41603 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A959 S41603
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
ASTM A959 S41603
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S41603 and GOST 5632 06Kh23N28?
ASTM A959 S41603 specifies P, S which are not specified for GOST 5632 06Kh23N28. GOST 5632 06Kh23N28 specifies Ni which is not specified for ASTM A959 S41603.
Can ASTM A959 S41603 be substituted with GOST 5632 06Kh23N28?
ASTM A959 S41603 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.