ASTM A959 S42010 vs ASTM A959 S42035

Close Alternative — 70.8% match based on chemical composition and mechanical property overlap.

ASTM A959 S42010 (ASTM A959:2011) and ASTM A959 S42035 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S42010 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while ASTM A959 S42035 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 S42010 is defined under ASTM International, originating from United States, while ASTM A959 S42035 is defined under ASTM International, originating from United States.

As per chemical composition, ASTM A959 S42010 vs ASTM A959 S42035 is a 70.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 70.8%.

Frequently Compared With ASTM A959 S42010:
IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
70.8%
MECHANICAL MATCH
No shared data
OVERALL
70.8%
Specifications
Property ASTM A959 S42010 ASTM A959 S42035
Standard ASTM A959:2011 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.15-0.30 <=0.08
Cr (%) 13.5-15.0 13.5-15.5
Mn (%) <=1.00 <=1.00
Mo (%) 0.40-0.85 0.20-1.20
Ni (%) 0.35-0.85 1.00-2.50
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Ti (%) Not specified 0.30-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
ASTM A959 S42010
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
ASTM A959 S42035
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can ASTM A959 S42010 Be Substituted With ASTM A959 S42035?
ASTM A959 S42010 and ASTM A959 S42035 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S42010
0 active listings and RFQs →
ASTM A959 S42035
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S42010 and ASTM A959 S42035?
ASTM A959 S42035 specifies Ti which is not specified for ASTM A959 S42010.
Can ASTM A959 S42010 be substituted with ASTM A959 S42035?
ASTM A959 S42010 and ASTM A959 S42035 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.