ASTM A959 S42035 vs EN 10088-2 X5CrNiMoTi15-2

Strong Match — 98.3% match based on chemical composition and mechanical property overlap.

ASTM A959 S42035 (ASTM A959:2011) and EN 10088-2 X5CrNiMoTi15-2 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S42035 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while EN 10088-2 X5CrNiMoTi15-2 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. ASTM A959 S42035 is defined under ASTM International, originating from United States, while EN 10088-2 X5CrNiMoTi15-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A959 S42035 vs EN 10088-2 X5CrNiMoTi15-2 is a 98.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.3%.

Frequently Compared With ASTM A959 S42035:
GOST 5632 08X18H10 GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
No shared data
OVERALL
98.3%
Specifications
Property ASTM A959 S42035 EN 10088-2 X5CrNiMoTi15-2
Standard ASTM A959:2011 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Cr (%) 13.5-15.5 13.5-15.5
Mn (%) <=1.00 <=1.00
Mo (%) 0.20-1.20 0.20-1.20
Ni (%) 1.00-2.50 1.00-2.50
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Ti (%) 0.30-0.50 0.30-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S42035 EN 10088-2 X5CrNiMoTi15-2
Tensile Strength Not specified 550-750 MPa
Condition Not specified Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Yield Strength Not specified >=400 MPa
Elongation Not specified >=16%
Typical Applications
ASTM A959 S42035
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
EN 10088-2 X5CrNiMoTi15-2
General purposes, hot or cold rolled sheet/plate and strip
Can ASTM A959 S42035 Be Substituted With EN 10088-2 X5CrNiMoTi15-2?
ASTM A959 S42035 and EN 10088-2 X5CrNiMoTi15-2 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X5CrNiMoTi15-2 is often considered as a substitute for ASTM A959 S42035 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S42035
0 active listings and RFQs →
EN 10088-2 X5CrNiMoTi15-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S42035 and EN 10088-2 X5CrNiMoTi15-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S42035 be substituted with EN 10088-2 X5CrNiMoTi15-2?
ASTM A959 S42035 and EN 10088-2 X5CrNiMoTi15-2 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X5CrNiMoTi15-2 is often considered as a substitute for ASTM A959 S42035 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.