ASTM A959 S44025 vs IS 6603 X110Cr17

Close Alternative — 82.1% match based on chemical composition and mechanical property overlap.

ASTM A959 S44025 (ASTM A959:2011) and IS 6603 X110Cr17 (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S44025 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 6603 X110Cr17 is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars. ASTM A959 S44025 is defined under ASTM International, originating from United States, while IS 6603 X110Cr17 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S44025 vs IS 6603 X110Cr17 is a 82.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.1%.

Frequently Compared With ASTM A959 S44025:
IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
82.1%
MECHANICAL MATCH
No shared data
OVERALL
82.1%
Specifications
Property ASTM A959 S44025 IS 6603 X110Cr17
Standard ASTM A959:2011 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) 0.95-1.10 0.95-1.20
Cr (%) 16.0-18.0 16.0-18.0
Cu (%) <=0.50 Not specified
Mn (%) 0.30-1.00 <=1.00
Mo (%) 0.40-0.65 <=0.75
Ni (%) <=0.75 <=0.60
P (%) <=0.025 <=0.040
S (%) <=0.025 <=0.030
Si (%) 0.30-1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S44025 IS 6603 X110Cr17
Hardness Not specified <=285 HB
Condition Not specified Soft annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; hardness as printed
Typical Applications
ASTM A959 S44025
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 6603 X110Cr17
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can ASTM A959 S44025 Be Substituted With IS 6603 X110Cr17?
ASTM A959 S44025 and IS 6603 X110Cr17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
ASTM A959 S44025
0 active listings and RFQs →
IS 6603 X110Cr17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S44025 and IS 6603 X110Cr17?
ASTM A959 S44025 specifies Cu which is not specified for IS 6603 X110Cr17.
Can ASTM A959 S44025 be substituted with IS 6603 X110Cr17?
ASTM A959 S44025 and IS 6603 X110Cr17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.