ASTM A959 S66286 vs IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB

Strong Match — 98.8% match based on chemical composition and mechanical property overlap.

ASTM A959 S66286 (ASTM A959:2011) and IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. ASTM A959 S66286 is typically used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1), while IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11). ASTM A959 S66286 is defined under ASTM International, originating from United States, while IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, ASTM A959 S66286 vs IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is a 98.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.8%.

Frequently Compared With ASTM A959 S66286:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo EN 10088-1 1.4006 EN 10088-1 1.4301 ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
98.8%
MECHANICAL MATCH
No shared data
OVERALL
98.8%
Specifications
Property ASTM A959 S66286 IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
Standard ASTM A959:2011 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
Al (%) <=0.35 <=0.35
B (%) 0.003-0.010 0.001-0.010
C (%) <=0.08 <=0.08
Cr (%) 13.5-16.0 13.5-16.0
Mn (%) <=2.00 <=2.00
Mo (%) 1.00-1.50 1.00-1.50
Ni (%) 24.0-27.0 24.0-27.0
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Ti (%) 1.90-2.35 1.90-2.35
V (%) 0.10-0.50 0.10-0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A959 S66286 IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
Reduction of Area, cold drawn and solution annealed (+AT+C+AT) Not specified >=65% (0.8 to 5 mm)
Tensile Strength, cold drawn and solution annealed (+AT+C+AT) Not specified <=780 MPa (0.8 to 2 mm) / <=730 MPa (over 2 to 5 mm)
Typical Applications
ASTM A959 S66286
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Can ASTM A959 S66286 Be Substituted With IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB?
ASTM A959 S66286 and IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is often considered as a substitute for ASTM A959 S66286 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
ASTM A959 S66286
0 active listings and RFQs →
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A959 S66286 and IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can ASTM A959 S66286 be substituted with IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB?
ASTM A959 S66286 and IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is often considered as a substitute for ASTM A959 S66286 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.