IS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB Steel: Specifications & Listings

IS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB: Cold heading quality austenitic stainless steel with molybdenum X04Ni25Cr15Ti2Mo1VB to IS 11169 (Part 2):2023, supplied as wire rod, bars or wire of 0.8 to 50 mm. Maximum tensile strength cold drawn and solution annealed is 780 MPa for the smallest sizes, lower for larger sizes.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB
Standard IS 11169 (Part 2):2023
ApplicationsCold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ISO 4980-662-86-X ISO 4954 International Not yet on M-EX
UNS S66286 ASTM A959 USA Not yet on M-EX
EN X6NiCrTiMoVB25-15-2 (1.4980) EN 10263 Europe Not yet on M-EX
JIS SUH660 JIS Japan Not yet on M-EX
GB/ISC S51525 GB China Not yet on M-EX
ASTM A959 S66286 ASTM A959:2011 USA No activity yet
ASTM A959 660 ASTM A959:2011 USA No activity yet
EN 10088-1 X5NiCrTiMoVB25-15-2 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X6NiCrTiMoVB25-15-2 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 660 ASTM A959:2011 Strong Match
ASTM A959 S66286 ASTM A959:2011 Strong Match
EN 10088-1 X5NiCrTiMoVB25-15-2 EN 10088-1:2014 Strong Match
EN 10088-1 X5NiCrTiMoVB25-15-2 EN 10088-1:2023 Strong Match
EN 10088-1 X6NiCrTiMoVB25-15-2 EN 10088-1:2014 Strong Match
EN 10088-1 X6NiCrTiMoVB25-15-2 EN 10088-1:2023 Strong Match
ASTM A959 622 ASTM A959:2011 Related Material
ASTM A959 662 ASTM A959:2011 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
Al B C Cr Mn Mo Ni P S Si Ti V
<=0.35 0.001-0.010 <=0.08 13.5-16.0 <=2.00 1.00-1.50 24.0-27.0 <=0.040 <=0.030 <=1.00 1.90-2.35 0.10-0.50
Mechanical Properties
Reduction of Area, cold drawn and solution annealed (+AT+C+AT) >=65% (0.8 to 5 mm)
Tensile Strength, cold drawn and solution annealed (+AT+C+AT) <=780 MPa (0.8 to 2 mm) / <=730 MPa (over 2 to 5 mm)

More data from IS 11169 (Part 2):2023

From the standard
Other composition limits from the table notes
Values
Maximum unless a range is given (ladle analysis)
Steel type
Austenitic with molybdenum
Titanium, aluminium, vanadium, boron
Ti 1.90 to 2.35, Al 0.35 max, V 0.10 to 0.50, B 0.001 to 0.010 percent
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 2):2023, Table 10 and its notes
Tensile strength and reduction of area by delivery condition by delivery condition and size
Delivery conditionDiameter (mm)Tensile strength, max (MPa)Reduction of area, min (%)
+AT+C+AT0.8 to 278065
+AT+C+ATover 2 to 573065
+AT+C+AT+LC0.8 to 283060
+AT+C+AT+LCover 2 to 578060
+AT+C+AT+LCover 5 to 1078060
+AT+C+AT+LCover 10 to 2578060
Codes: +AT solution annealed, +A soft annealed, +PE peeled, +C cold drawn, +LC skin passed. Diameter ranges are over the first figure up to and including the second. No reduction of area is specified for +AT+C. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 2):2023, Table 11

Active IS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):2023 X04Ni25Cr15Ti2Mo1VB at this time.

Register for Alerts