BS 970 (Part 1) 080A57 vs AISI 1055

Strong Match — 93.8% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 080A57 (BS 970 (Part 1):1983) and AISI 1055 are both steel grades. Both fall under the Carbon Steel category. BS 970 (Part 1) 080A57 is typically used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6., while AISI 1055 is commonly used for springs, hand tools, high strength wire. BS 970 (Part 1) 080A57 is defined under British Standards (BS), originating from United Kingdom, while AISI 1055 is defined under AISI, originating from United States.

As per chemical composition, BS 970 (Part 1) 080A57 vs AISI 1055 is a 93.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.8%.

Frequently Compared With BS 970 (Part 1) 080A57:
BS 970 (Part 1) 060A57 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
93.8%
MECHANICAL MATCH
No shared data
OVERALL
93.8%
Specifications
Property BS 970 (Part 1) 080A57 AISI 1055
Standard BS 970 (Part 1):1983 AISI
Category Carbon Steel Carbon Steel
C (%) 0.55-0.60 0.50–0.60
Mn (%) 0.70-0.90 0.60–0.90
P (%) <=0.050 ≤0.030
S (%) <=0.050 ≤0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 080A57 AISI 1055
Condition Not specified Hot Rolled
Tensile Strength Not specified 700-750 MPa
Yield Strength Not specified 380-450 MPa
Elongation Not specified 12-16%
Hardness Not specified 197-220 HB
Typical Applications
BS 970 (Part 1) 080A57
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
AISI 1055
Springs, hand tools, high strength wire
Can BS 970 (Part 1) 080A57 Be Substituted With AISI 1055?
BS 970 (Part 1) 080A57 and AISI 1055 overlap closely enough on chemistry and mechanical properties that AISI 1055 is often considered as a substitute for BS 970 (Part 1) 080A57 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 080A57
No active listings currently.
AISI 1055
Round Bar → (3 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 6400–7000 mm (251.97–275.59 in)
On M-EX Right Now
BS 970 (Part 1) 080A57
0 active listings and RFQs →
AISI 1055
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 080A57 and AISI 1055?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 080A57 be substituted with AISI 1055?
BS 970 (Part 1) 080A57 and AISI 1055 overlap closely enough on chemistry and mechanical properties that AISI 1055 is often considered as a substitute for BS 970 (Part 1) 080A57 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.