BS 970 (Part 1) 316S13 vs EN 10088-2 X2CrNiMoN17-13-3

Strong Match — 90.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 316S13 (BS 970 (Part 1):1983) and EN 10088-2 X2CrNiMoN17-13-3 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 316S13 is typically used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition)., while EN 10088-2 X2CrNiMoN17-13-3 is commonly used for general purposes, hot or cold rolled sheet/plate and strip. BS 970 (Part 1) 316S13 is defined under British Standards (BS), originating from United Kingdom, while EN 10088-2 X2CrNiMoN17-13-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 1) 316S13 vs EN 10088-2 X2CrNiMoN17-13-3 is a 90.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.7%.

Frequently Compared With BS 970 (Part 1) 316S13:
EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4006 EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
90.7%
MECHANICAL MATCH
No shared data
OVERALL
90.7%
Specifications
Property BS 970 (Part 1) 316S13 EN 10088-2 X2CrNiMoN17-13-3
Standard BS 970 (Part 1):1983 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Cr (%) 16.5-18.5 16.5-18.5
Mo (%) 2.50-3.00 2.50-3.00
Ni (%) 11.5-14.5 11.0-14.0
N (%) Not specified 0.12-0.22
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 316S13 EN 10088-2 X2CrNiMoN17-13-3
Tensile Strength Not specified 580-780 MPa
Yield Strength Not specified >=300 MPa
Elongation Not specified >=35%
Condition Not specified Solution annealed (+AT), cold rolled strip, up to 8 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
BS 970 (Part 1) 316S13
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
EN 10088-2 X2CrNiMoN17-13-3
General purposes, hot or cold rolled sheet/plate and strip
Key Differences
Can BS 970 (Part 1) 316S13 Be Substituted With EN 10088-2 X2CrNiMoN17-13-3?
BS 970 (Part 1) 316S13 and EN 10088-2 X2CrNiMoN17-13-3 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrNiMoN17-13-3 is often considered as a substitute for BS 970 (Part 1) 316S13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 316S13
0 active listings and RFQs →
EN 10088-2 X2CrNiMoN17-13-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 316S13 and EN 10088-2 X2CrNiMoN17-13-3?
EN 10088-2 X2CrNiMoN17-13-3 specifies N which is not specified for BS 970 (Part 1) 316S13.
Can BS 970 (Part 1) 316S13 be substituted with EN 10088-2 X2CrNiMoN17-13-3?
BS 970 (Part 1) 316S13 and EN 10088-2 X2CrNiMoN17-13-3 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrNiMoN17-13-3 is often considered as a substitute for BS 970 (Part 1) 316S13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.