BS 970 (Part 1) 321S31 vs IS 11169 (Part 2) X04Cr18Ni10Ti

Strong Match — 100% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 321S31 (BS 970 (Part 1):1983) and IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):1989) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 321S31 is typically used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition)., while IS 11169 (Part 2) X04Cr18Ni10Ti is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1). BS 970 (Part 1) 321S31 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 321S31 vs IS 11169 (Part 2) X04Cr18Ni10Ti is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With BS 970 (Part 1) 321S31:
EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H ASTM A959 .- EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property BS 970 (Part 1) 321S31 IS 11169 (Part 2) X04Cr18Ni10Ti
Standard BS 970 (Part 1):1983 IS 11169 (Part 2):1989
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.0
Mn (%) <=2.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) 9.0-12.0 9.0-12.0
Ti (%) 5C-0.80 >=5xC, <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 321S31 IS 11169 (Part 2) X04Cr18Ni10Ti
Yield Strength (0.2% proof) Not specified >=205 MPa
Tensile Strength Not specified 500-750 MPa
Elongation Not specified >=40%
Impact (U-notch 5 mm) Not specified >=60 J
Condition Not specified Quenched reference test piece (Table 6 treatment)
Typical Applications
BS 970 (Part 1) 321S31
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Can BS 970 (Part 1) 321S31 Be Substituted With IS 11169 (Part 2) X04Cr18Ni10Ti?
BS 970 (Part 1) 321S31 and IS 11169 (Part 2) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr18Ni10Ti is often considered as a substitute for BS 970 (Part 1) 321S31 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 321S31
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr18Ni10Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 321S31 and IS 11169 (Part 2) X04Cr18Ni10Ti?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 321S31 be substituted with IS 11169 (Part 2) X04Cr18Ni10Ti?
BS 970 (Part 1) 321S31 and IS 11169 (Part 2) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X04Cr18Ni10Ti is often considered as a substitute for BS 970 (Part 1) 321S31 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.