BS 970 (Part 1) 430S17 vs IS 1570 (Part 7) 12Cr13H
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
BS 970 (Part 1) 430S17 (BS 970 (Part 1):1983) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
BS 970 (Part 1) 430S17 is typically used for stainless and heat resisting steel for mechanical and allied engineering purposes (table 13)., while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
BS 970 (Part 1) 430S17 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, BS 970 (Part 1) 430S17 vs IS 1570 (Part 7) 12Cr13H is a 79.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
BS 970 (Part 1) 430S17
IS 1570 (Part 7) 12Cr13H
Tensile Strength
Not specified
470-670 MPa
Yield Strength
Not specified
>=265 MPa (0.2 % proof stress)
Elongation
Not specified
>=20%
Condition
Not specified
Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
BS 970 (Part 1) 430S17
Stainless and heat resisting steel for mechanical and allied engineering purposes (Table 13).
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can BS 970 (Part 1) 430S17 Be Substituted With IS 1570 (Part 7) 12Cr13H?
BS 970 (Part 1) 430S17 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between BS 970 (Part 1) 430S17 and IS 1570 (Part 7) 12Cr13H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 430S17 be substituted with IS 1570 (Part 7) 12Cr13H?
BS 970 (Part 1) 430S17 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.