BS 970 (Part 1) 535A99 vs EN 10028-2 10CrMo9-10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 535A99 (BS 970 (Part 1):1983) and EN 10028-2 10CrMo9-10 (EN 10028-2:2017) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 535A99 is typically used for used for aircraft fittings, gears, high-strength shafts, crankshafts, heavy-duty fasteners, and transmission parts., while EN 10028-2 10CrMo9-10 is commonly used for flat products for pressure purposes. BS 970 (Part 1) 535A99 is defined under British Standards (BS), originating from United Kingdom, while EN 10028-2 10CrMo9-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 1) 535A99 vs EN 10028-2 10CrMo9-10 is a 59.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 1) 535A99:
NF A35-565 100C6 UNI 11234 100Cr6 GOST 4543 12HN3A GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
59.8%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 1) 535A99 EN 10028-2 10CrMo9-10
Standard BS 970 (Part 1):1983 EN 10028-2:2017
Category Alloy Steel Alloy Steel
C (%) 0.95-1.10 0.08-0.14
Mn (%) 0.40-0.70 0.40-0.80
P (%) <=0.035 <=0.020
S (%) <=0.040 <=0.010
Cr (%) 1.20-1.60 2.00-2.50
Si (%) Not specified <=0.50
N (%) Not specified <=0.012
Cu (%) Not specified <=0.30
Mo (%) Not specified 0.90-1.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 535A99 EN 10028-2 10CrMo9-10
Tensile Strength Not specified 480-630 MPa
Yield Strength Not specified >=310 MPa
Elongation Not specified >=18%
Condition Not specified Usual delivery condition normalized and tempered (+NT), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A
Typical Applications
BS 970 (Part 1) 535A99
Used for aircraft fittings, gears, high-strength shafts, crankshafts, heavy-duty fasteners, and transmission parts.
EN 10028-2 10CrMo9-10
Flat products for pressure purposes
Key Differences
Can BS 970 (Part 1) 535A99 Be Substituted With EN 10028-2 10CrMo9-10?
BS 970 (Part 1) 535A99 and EN 10028-2 10CrMo9-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 535A99
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5200–6400 mm (204.72–251.97 in)
EN 10028-2 10CrMo9-10
No active listings currently.
On M-EX Right Now
BS 970 (Part 1) 535A99
2 active listings and RFQs →
EN 10028-2 10CrMo9-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 535A99 and EN 10028-2 10CrMo9-10?
EN 10028-2 10CrMo9-10 specifies Si, N, Cu, Mo which are not specified for BS 970 (Part 1) 535A99.
Can BS 970 (Part 1) 535A99 be substituted with EN 10028-2 10CrMo9-10?
BS 970 (Part 1) 535A99 and EN 10028-2 10CrMo9-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.