BS 970 (Part 1) 535A99 vs GB/T 3077 12Cr2Ni4A

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 535A99 (BS 970 (Part 1):1983) and GB/T 3077 12Cr2Ni4A (GB/T 3077-2015) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 535A99 is typically used for used for aircraft fittings, gears, high-strength shafts, crankshafts, heavy-duty fasteners, and transmission parts., while GB/T 3077 12Cr2Ni4A is commonly used for used for gears, shafts, pinions, aircraft parts, heavy-duty bearings, and transmission components.. BS 970 (Part 1) 535A99 is defined under British Standards (BS), originating from United Kingdom, while GB/T 3077 12Cr2Ni4A is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, BS 970 (Part 1) 535A99 vs GB/T 3077 12Cr2Ni4A is a 70.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 1) 535A99:
NF A35-565 100C6 UNI 11234 100Cr6 GOST 4543 12HN3A IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
70.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 1) 535A99 GB/T 3077 12Cr2Ni4A
Standard BS 970 (Part 1):1983 GB/T 3077-2015
Category Alloy Steel Alloy Steel
C (%) 0.95-1.10 0.10-0.15
Mn (%) 0.40-0.70 0.30-0.60
P (%) <=0.035 0.025 max
S (%) <=0.040 0.025 max
Cr (%) 1.20-1.60 1.25-1.65
Si (%) Not specified 0.17-0.37
Ni (%) Not specified 3.25-3.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 535A99 GB/T 3077 12Cr2Ni4A
Tensile Strength Not specified 980-1180 MPa
Yield Strength Not specified 785-980 MPa
Elongation Not specified 10-14%
Hardness Not specified 58-62 HRC (case)
Typical Applications
BS 970 (Part 1) 535A99
Used for aircraft fittings, gears, high-strength shafts, crankshafts, heavy-duty fasteners, and transmission parts.
GB/T 3077 12Cr2Ni4A
Used for gears, shafts, pinions, aircraft parts, heavy-duty bearings, and transmission components.
Key Differences
Can BS 970 (Part 1) 535A99 Be Substituted With GB/T 3077 12Cr2Ni4A?
BS 970 (Part 1) 535A99 and GB/T 3077 12Cr2Ni4A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 535A99
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5200–6400 mm (204.72–251.97 in)
GB/T 3077 12Cr2Ni4A
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5000–6600 mm (196.85–259.84 in)
On M-EX Right Now
BS 970 (Part 1) 535A99
2 active listings and RFQs →
GB/T 3077 12Cr2Ni4A
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 535A99 and GB/T 3077 12Cr2Ni4A?
GB/T 3077 12Cr2Ni4A specifies Si, Ni which are not specified for BS 970 (Part 1) 535A99.
Can BS 970 (Part 1) 535A99 be substituted with GB/T 3077 12Cr2Ni4A?
BS 970 (Part 1) 535A99 and GB/T 3077 12Cr2Ni4A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.