BS 970 (Part 1) 832H13 vs IS 4367 07Cr4Mo6

Related Material — 64.7% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 832H13 (BS 970 (Part 1):1983) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 832H13 is defined under British Standards (BS), originating from United Kingdom, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 1) 832H13 vs IS 4367 07Cr4Mo6 is a 64.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 64.7%.

Frequently Compared With BS 970 (Part 1) 832H13:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
64.7%
MECHANICAL MATCH
No shared data
OVERALL
64.7%
Specifications
Property BS 970 (Part 1) 832H13 IS 4367 07Cr4Mo6
Standard BS 970 (Part 1):1983 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.10-0.16 <=0.12
Mn (%) 0.35-0.60 0.40-0.70
Cr (%) 0.70-1.00 0.70-1.10
Mo (%) 0.10-0.25 0.45-0.65
Ni (%) 3.00-3.75 <=0.30
P (%) <=0.035 <=0.035
S (%) <=0.040 <=0.035
Si (%) Not specified 0.15-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 832H13 IS 4367 07Cr4Mo6
Tensile Strength Not specified 380-550 MPa
Yield Strength Not specified 225 MPa min
Elongation Not specified >=19%
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Condition Not specified Normalised and tempered, ruling section up to 40 mm
Typical Applications
BS 970 (Part 1) 832H13
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can BS 970 (Part 1) 832H13 Be Substituted With IS 4367 07Cr4Mo6?
BS 970 (Part 1) 832H13 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 (Part 1) 832H13
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 832H13 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies Si which is not specified for BS 970 (Part 1) 832H13.
Can BS 970 (Part 1) 832H13 be substituted with IS 4367 07Cr4Mo6?
BS 970 (Part 1) 832H13 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.