BS 970 (Part 1):1991 310S31 Steel: Specifications & Listings

BS 970 (Part 1):1991 310S31: 310S31 is a austenitic steel specified in BS 970 Part 1:1991 (category 1).

Category: Stainless Steel
Grade Details
GradeBS 970 (Part 1):1991 310S31
Standard BS 970 (Part 1):1991
ApplicationsAustenitic stainless and heat resisting steel (section five)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 310S ASTM A959:2011 USA No activity yet
ASTM A959 310H ASTM A959:2011 USA No activity yet
ASTM A959 310Cb ASTM A959:2011 USA No activity yet
ASTM A959 310HCb ASTM A959:2011 USA No activity yet
ASTM A959 310HCbN ASTM A959:2011 USA No activity yet
BS 970 (Part 3) 310S31 BS 970 (Part 3):1991 UK No activity yet
ASTM A959 SS310 ASTM A959:2011 USA 3 listings, 0 RFQs →
EN 10088-1 X8CrNi25-21 EN 10088-1:2014 Europe (CEN) 3 listings, 0 RFQs →
ASTM A959 314 ASTM A959:2011 USA No activity yet
EN 10088-1 X15CrNiSi25-21 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
BS 970 (Part 3) 310S31 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 310S31 BS 970 (Part 1):1983 Strong Match
ASTM A959 SS310 ASTM A959:2011 Strong Match
ASTM A959 310S ASTM A959:2011 Strong Match
ASTM A959 310Cb ASTM A959:2011 Strong Match
EN 10088-1 X8CrNi25-21 EN 10088-1:2014 Strong Match
ASTM A959 310H ASTM A959:2011 Strong Match
ASTM A959 310HCb ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Ni
<=0.15 <=1.5 <=2.0 <=0.045 <=0.030 24.0-26.0 19.0-22.0
Mechanical Properties
Condition Softened, 1000-1100 deg C
Tensile Strength 510 MPa min
Yield Strength 205 MPa min (0.2% proof)
Elongation 40 % min
Hardness 207 HB max

More data from BS 970 (Part 1):1991

From the standard
Other composition limits
Category
Category 1 steel (note 7)
Maximum unless a range is stated.
Source: BS 970 (Part 1):1991, Table 11
Properties in the softened condition
Softening temperature
1000-1100 deg C
Maximum section
160 mm
Tensile strength, min
510 MPa
Elongation, min
40 %
Rp0.2, min (when specified)
205 MPa
Rp1.0, min (when specified)
240 MPa
Hardness, max
207 HB
Straightening by reeling or cold rectification can increase the surface hardness above the specified maximum (note 36). 1 N/mm2 = 1 MPa.
Source: BS 970 (Part 1):1991, Table 11

Active BS 970 (Part 1):1991 310S31 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active BS 970 (Part 1):1991 310S31 listings at this time.

Register for Alerts

Buyer RFQs for BS 970 (Part 1):1991 310S31

+ Post an RFQ for this grade

No open buyer requirements for BS 970 (Part 1):1991 310S31 at this time.

Register for Alerts