BS 970 (Part 1) 637H17 vs BS 970 (Part 1) 635M15

Strong Match — 85.3% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 637H17 (BS 970 (Part 1):1991) and BS 970 (Part 1) 635M15 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 637H17 is typically used for case hardening steel (section four), while BS 970 (Part 1) 635M15 is commonly used for case hardening steel (section four). BS 970 (Part 1) 637H17 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 635M15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 (Part 1) 637H17 vs BS 970 (Part 1) 635M15 is a 85.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.3%.

Frequently Compared With BS 970 (Part 1) 637H17:
IS 11169 (Part 1) 10Ni5Cr4 EN 10084 10NiCr5-4 GOST 4543 12HN3A IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6
Match Breakdown
CHEMISTRY MATCH
85.3%
MECHANICAL MATCH
No shared data
OVERALL
85.3%
Specifications
Property BS 970 (Part 1) 637H17 BS 970 (Part 1) 635M15
Standard BS 970 (Part 1):1991 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.14-0.20 0.12-0.18
Mn (%) 0.60-0.90 0.60-0.90
Cr (%) 0.60-1.00 0.40-0.80
Ni (%) 0.85-1.25 0.70-1.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 637H17 BS 970 (Part 1) 635M15
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 770 MPa min
Elongation Not specified 12 % min
Typical Applications
BS 970 (Part 1) 637H17
Case hardening steel (section four)
BS 970 (Part 1) 635M15
Case hardening steel (section four)
Can BS 970 (Part 1) 637H17 Be Substituted With BS 970 (Part 1) 635M15?
BS 970 (Part 1) 637H17 and BS 970 (Part 1) 635M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 635M15 is often considered as a substitute for BS 970 (Part 1) 637H17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 1) 637H17
0 active listings and RFQs →
BS 970 (Part 1) 635M15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 637H17 and BS 970 (Part 1) 635M15?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 1) 637H17 be substituted with BS 970 (Part 1) 635M15?
BS 970 (Part 1) 637H17 and BS 970 (Part 1) 635M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 635M15 is often considered as a substitute for BS 970 (Part 1) 637H17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.