BS 970 EN16 vs UNI 11234 100Cr6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 EN16 (BS 970:1955) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. BS 970 EN16 is typically used for high tensile bolts, studs, general engineering, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. BS 970 EN16 is defined under British Standards (BS), originating from United Kingdom, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, BS 970 EN16 vs UNI 11234 100Cr6 is a 64.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 EN16:
IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
64.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property BS 970 EN16 UNI 11234 100Cr6
Standard BS 970:1955 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.30-0.40 0.93-1.05
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 1.30-1.80 0.25-0.45
Mo (%) 0.20-0.35 Not specified
S (%) <=0.050 <=0.025
P (%) <=0.050 <=0.025
Cr (%) Not specified 1.35-1.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN16 UNI 11234 100Cr6
Tensile Strength ≥695 MPa (45 tons/sq in, converted) 750-1000 MPa
Yield Strength ≥525 MPa (34 tons/sq in, converted) 400-600 MPa
Elongation ≥22% 10-14 %
Hardness 201-255 HB 60-64 HRC
Condition Hardened and tempered R, ruling section 6 in (lowest-strength condition of the standard) Not specified
Typical Applications
BS 970 EN16
High tensile bolts, studs, general engineering
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can BS 970 EN16 Be Substituted With UNI 11234 100Cr6?
BS 970 EN16 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 EN16
Round Bar → (6 listings)
Diameter: 55–70 mm (2.17–2.76 in)
Length: 5400–6900 mm (212.6–271.65 in)
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
BS 970 EN16
6 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN16 and UNI 11234 100Cr6?
BS 970 EN16 specifies Mo which is not specified for UNI 11234 100Cr6. UNI 11234 100Cr6 specifies Cr which is not specified for BS 970 EN16.
Can BS 970 EN16 be substituted with UNI 11234 100Cr6?
BS 970 EN16 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.