BS 970 EN19 vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 41.9% match based on chemical composition and mechanical property overlap.

BS 970 EN19 (BS 970:1955) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. BS 970 EN19 is typically used for gears, shafts, bolts, automotive axles, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. BS 970 EN19 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 EN19 vs IS 1570 (Part 7) 10Cr36Mo10H is a 62.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 41.9%.

Frequently Compared With BS 970 EN19:
UNI 11234 100Cr6 NF A35-565 100C6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
62.9%
MECHANICAL MATCH
0%
OVERALL
41.9%
Specifications
Property BS 970 EN19 IS 1570 (Part 7) 10Cr36Mo10H
Standard BS 970:1955 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 <=0.15
Si (%) 0.10-0.35 0.25-1.0
Mn (%) 0.50-0.80 0.30-0.60
Cr (%) 0.90-1.50 8.00-10.00
Mo (%) 0.20-0.40 0.90-1.10
S (%) <=0.050 <=0.030
P (%) <=0.050 <=0.040
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN19 IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength ≥695 MPa (45 tons/sq in, converted) 410-560 MPa
Yield Strength ≥525 MPa (34 tons/sq in, converted) >=135 MPa (0.2 % proof stress)
Elongation ≥22% >=20%
Hardness 201-255 HB Not specified
Condition Hardened and tempered R, ruling section 6 in (lowest-strength condition of the standard) Pipes, A, thickness - (first row of Table 3)
Typical Applications
BS 970 EN19
Gears, shafts, bolts, automotive axles
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can BS 970 EN19 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
BS 970 EN19 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 EN19
Round Bar → (24 listings)
Diameter: 40–75 mm (1.57–2.95 in)
Length: 4900–6900 mm (192.91–271.65 in)
Forging → (4 listings)
Diameter: 180–200 mm (7.09–7.87 in)
Length: 500–1700 mm (19.69–66.93 in)
Flat Bar → (3 listings)
Thickness: 40–40 mm (1.57–1.57 in)
Width: 120–120 mm (4.72–4.72 in)
Length: 3100–3900 mm (122.05–153.54 in)
Hex Bar → (3 listings)
Across Flats: 40–40 mm (1.57–1.57 in)
Length: 2500–3100 mm (98.43–122.05 in)
IS 1570 (Part 7) 10Cr36Mo10H
No active listings currently.
On M-EX Right Now
BS 970 EN19
34 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN19 and IS 1570 (Part 7) 10Cr36Mo10H?
IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for BS 970 EN19.
Can BS 970 EN19 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
BS 970 EN19 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.