BS 970 EN202 vs BS 970 (Part 1) 216M28

Close Alternative — 84.9% match based on chemical composition and mechanical property overlap.

BS 970 EN202 (BS 970:1955) and BS 970 (Part 1) 216M28 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Free Machining Steel category. BS 970 EN202 is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. for this type in cold drawn condition see en 7a., while BS 970 (Part 1) 216M28 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. BS 970 EN202 is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 216M28 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN202 vs BS 970 (Part 1) 216M28 is a 85.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.9%.

Frequently Compared With BS 970 EN202:
SAE J403 1132 IS 1570 (Part 3) 10C8S10 SAE J403 1117 SAE J403 1117 SAE J403 1118 SAE J403 1118 SAE J403 1126 SAE J403 1126 IS 4432 10C8S10 SAE J403 1117 SAE J403 1118 SAE J403 1126
Match Breakdown
CHEMISTRY MATCH
85.6%
MECHANICAL MATCH
No shared data
OVERALL
84.9%
Specifications
Property BS 970 EN202 BS 970 (Part 1) 216M28
Standard BS 970:1955 BS 970 (Part 1):1983
Category Free Machining Steel Free Machining Steel
C (%) <=0.18 0.24-0.32
Si (%) 0.05-0.35 <=0.25
Mn (%) 1.20-1.50 1.10-1.50
S (%) 0.10-0.18 0.12-0.20
P (%) <=0.050 <=0.060
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN202 BS 970 (Part 1) 216M28
Tensile Strength ≥587 MPa (38 tons/sq in, converted) Not specified
Elongation ≥20% Not specified
Condition Core, after heat treatment (lowest-strength condition of the standard) Not specified
Typical Applications
BS 970 EN202
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars. For this type in cold drawn condition see En 7A.
BS 970 (Part 1) 216M28
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Can BS 970 EN202 Be Substituted With BS 970 (Part 1) 216M28?
BS 970 EN202 and BS 970 (Part 1) 216M28 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
BS 970 EN202
0 active listings and RFQs →
BS 970 (Part 1) 216M28
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN202 and BS 970 (Part 1) 216M28?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 EN202 be substituted with BS 970 (Part 1) 216M28?
BS 970 EN202 and BS 970 (Part 1) 216M28 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.