BS 970 EN2E vs BS 970 (Part 1) 045M10

Related Material — 56.9% match based on chemical composition and mechanical property overlap.

BS 970 EN2E (BS 970:1955) and BS 970 (Part 1) 045M10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. BS 970 EN2E is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining, while BS 970 (Part 1) 045M10 is commonly used for case hardening steel (section four). BS 970 EN2E is defined under British Standards (BS), originating from United Kingdom, while BS 970 (Part 1) 045M10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, BS 970 EN2E vs BS 970 (Part 1) 045M10 is a 85.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 56.9%.

Frequently Compared With BS 970 EN2E:
BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A45 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 060A40
Match Breakdown
CHEMISTRY MATCH
85.3%
MECHANICAL MATCH
0%
OVERALL
56.9%
Specifications
Property BS 970 EN2E BS 970 (Part 1) 045M10
Standard BS 970:1955 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) <=0.15 0.07-0.13
Si (%) 0.10-0.35 Not specified
Mn (%) <=0.50 0.30-0.60
S (%) <=0.050 Not specified
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN2E BS 970 (Part 1) 045M10
Tensile Strength ≥309 MPa (20 tons/sq in, converted) 430 MPa min
Elongation ≥28% 18 % min
Hardness ≤120 HB Not specified
Condition , ruling section 6 in (lowest-strength condition of the standard) Case hardened, 19 mm test bar
Typical Applications
BS 970 EN2E
Bars and billets for forging; forgings and drop-forgings; bars for machining
BS 970 (Part 1) 045M10
Case hardening steel (section four)
Key Differences
Can BS 970 EN2E Be Substituted With BS 970 (Part 1) 045M10?
BS 970 EN2E and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
BS 970 EN2E
0 active listings and RFQs →
BS 970 (Part 1) 045M10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN2E and BS 970 (Part 1) 045M10?
BS 970 EN2E specifies Si, S, P which are not specified for BS 970 (Part 1) 045M10.
Can BS 970 EN2E be substituted with BS 970 (Part 1) 045M10?
BS 970 EN2E and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.