Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
BS 970 EN53 (BS 970:1955) and IS 6911 X07Cr17 (IS 6911:1992) are both steel grades.
Both fall under the Stainless Steel category.
BS 970 EN53 is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars., while IS 6911 X07Cr17 is commonly used for stainless and heat-resisting steel plate, sheet and strip (clause 1.1).
BS 970 EN53 is defined under British Standards (BS), originating from United Kingdom, while IS 6911 X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, BS 970 EN53 vs IS 6911 X07Cr17 is a 72.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
BS 970 EN53
IS 6911 X07Cr17
Bend Test (180 deg)
Not specified
Mandrel diameter 2 x thickness
Elongation (50 mm, annealed)
Not specified
>=18%
Hardness (annealed, max)
Not specified
192 HBS, 88 HRB
Tensile Strength (annealed)
Not specified
>=440 MPa
Yield Strength (0.2% proof, annealed)
Not specified
>=250 MPa
Typical Applications
BS 970 EN53
Bars and billets for forging; forgings and drop-forgings; bars for machining; bright bars.
IS 6911 X07Cr17
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Can BS 970 EN53 Be Substituted With IS 6911 X07Cr17?
BS 970 EN53 and IS 6911 X07Cr17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between BS 970 EN53 and IS 6911 X07Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 EN53 be substituted with IS 6911 X07Cr17?
BS 970 EN53 and IS 6911 X07Cr17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.