IS 6911:1992 X07Cr17 Steel: Specifications & Listings

IS 6911:1992 X07Cr17: Ferritic stainless steel X07Cr17 (numerical symbol 430) to IS 6911:1992 (reaffirmed 1998), made as plate, sheet and strip and normally supplied annealed and descaled. Minimum tensile strength annealed is 440 MPa with 0.2% proof stress of 250 MPa.

Category: Stainless Steel
Grade Details
GradeIS 6911:1992 X07Cr17
Standard IS 6911:1992
ApplicationsStainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 1570 (Part 5) X07Cr17 IS 1570 (Part 5):1985 India No activity yet
IS 11169 (Part 2) X07Cr17 IS 11169 (Part 2):1989 India No activity yet
ASTM A959 430Ti ASTM A959:2011 USA No activity yet
ASTM A959 442 ASTM A959:2011 USA No activity yet
ASTM A959 443 ASTM A959:2011 USA No activity yet
BS 970 (Part 1) 430S17 BS 970 (Part 1):1991 UK No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
BS 970 EN60 BS 970:1955 Strong Match
BS 970 (Part 1) 430S17 BS 970 (Part 1):1991 Strong Match
BS 970 (Part 3) 430S17 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 430S17 BS 970 (Part 1):1983 Strong Match
ASTM A959 430Ti ASTM A959:2011 Strong Match
ASTM A959 442 ASTM A959:2011 Strong Match
ASTM A959 443 ASTM A959:2011 Strong Match
EN 10088-1 X6CrNi17-1 EN 10088-1:2014 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Cr Mn Ni P S Si
<=0.12 16.0-18.0 <=1.0 <=0.50 <=0.040 <=0.030 <=1.0
Mechanical Properties
Bend Test (180 deg) Mandrel diameter 2 x thickness
Elongation (50 mm, annealed) >=18%
Hardness (annealed, max) 192 HBS, 88 HRB
Tensile Strength (annealed) >=440 MPa
Yield Strength (0.2% proof, annealed) >=250 MPa

More data from IS 6911:1992

From the standard
Other composition limits from Table 1 and its note
Steel type
Ferritic
Numerical symbol (ISS)
430
Values
Maximum unless a range is given (ladle analysis)
Element not specified, Molybdenum, max
0.30
Element not specified, Copper, max
0.30
Elements not listed in Table 1 are not added to the steel except to finish the heat, and then only within the limits shown.
Source: IS 6911:1992, Table 1 and its note
Recommended heat treatment Table 3
TreatmentTemperature (deg C)Cooling medium
Annealing, A750 to 850air or water
Recommended heat treatment (clause 8.3). Austenitic steels are supplied solution annealed and descaled; ferritic and martensitic steels annealed and descaled, unless agreed otherwise.
Source: IS 6911:1992, Table 3

Active IS 6911:1992 X07Cr17 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 6911:1992 X07Cr17 listings at this time.

Register for Alerts

Buyer RFQs for IS 6911:1992 X07Cr17

+ Post an RFQ for this grade

No open buyer requirements for IS 6911:1992 X07Cr17 at this time.

Register for Alerts