Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
BS 970 (Part 3) 226M44 (BS 970 (Part 3):1991) and IS 4432 10C8S10 (IS 4432:1988) are both steel grades.
Both fall under the Free Machining Steel category.
BS 970 (Part 3) 226M44 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; free-cutting steel (table 12), while IS 4432 10C8S10 is commonly used for forgings and fabrication of case-hardened machine or automobile parts.
BS 970 (Part 3) 226M44 is defined under British Standards (BS), originating from United Kingdom, while IS 4432 10C8S10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, BS 970 (Part 3) 226M44 vs IS 4432 10C8S10 is a 75% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
BS 970 (Part 3) 226M44
IS 4432 10C8S10
Core Tensile Strength
Not specified
600-850 MPa (16 mm) / 550-800 MPa (30 mm)
Core Yield Strength
Not specified
>=400 MPa (16 mm) / >=330 MPa (30 mm)
Core Elongation
Not specified
>=12% (16 mm) / >=14% (30 mm)
Core Reduction of Area
Not specified
>=35% (16 mm) / >=40% (30 mm)
Hardness, annealed (A)
Not specified
<=150 HB
Typical Applications
BS 970 (Part 3) 226M44
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; free-cutting steel (Table 12)
IS 4432 10C8S10
Forgings and fabrication of case-hardened machine or automobile parts
Can BS 970 (Part 3) 226M44 Be Substituted With IS 4432 10C8S10?
BS 970 (Part 3) 226M44 and IS 4432 10C8S10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between BS 970 (Part 3) 226M44 and IS 4432 10C8S10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 3) 226M44 be substituted with IS 4432 10C8S10?
BS 970 (Part 3) 226M44 and IS 4432 10C8S10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.