BS 970 (Part 3) 416S37 vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 416S37 (BS 970 (Part 3):1991) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 3) 416S37 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (table 17), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. BS 970 (Part 3) 416S37 is defined under British Standards (BS), originating from United Kingdom, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 3) 416S37 vs EN 10088-1 1.4006 is a 58.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 3) 416S37:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
58.9%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 3) 416S37 EN 10088-1 1.4006
Standard BS 970 (Part 3):1991 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.20-0.28 0.08–0.15
Si (%) <=1.0 ≤1.00
Mn (%) <=1.5 ≤1.50
P (%) <=0.060 Not specified
S (%) 0.15-0.35 Not specified
Cr (%) 12.0-14.0 11.5–13.5
Mo (%) <=0.60 Not specified
Ni (%) <=1.00 ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 416S37 EN 10088-1 1.4006
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
BS 970 (Part 3) 416S37
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (Table 17)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can BS 970 (Part 3) 416S37 Be Substituted With EN 10088-1 1.4006?
BS 970 (Part 3) 416S37 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 3) 416S37
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
BS 970 (Part 3) 416S37
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 416S37 and EN 10088-1 1.4006?
BS 970 (Part 3) 416S37 specifies P, S, Mo which are not specified for EN 10088-1 1.4006.
Can BS 970 (Part 3) 416S37 be substituted with EN 10088-1 1.4006?
BS 970 (Part 3) 416S37 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.