BS 970 (Part 3) 416S37 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 416S37 (BS 970 (Part 3):1991) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 3) 416S37 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (table 17), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. BS 970 (Part 3) 416S37 is defined under British Standards (BS) (United Kingdom).

As per chemical composition, BS 970 (Part 3) 416S37 vs GOST 5632 06Kh23N28 is a 53.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 3) 416S37:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
53.5%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property BS 970 (Part 3) 416S37 GOST 5632 06Kh23N28
Standard BS 970 (Part 3):1991 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.20-0.28 ≤0.06
Si (%) <=1.0 ≤0.80
Mn (%) <=1.5 ≤2.00
P (%) <=0.060 Not specified
S (%) 0.15-0.35 Not specified
Cr (%) 12.0-14.0 22.0–25.0
Mo (%) <=0.60 Not specified
Ni (%) <=1.00 26.0–29.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 416S37 GOST 5632 06Kh23N28
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
BS 970 (Part 3) 416S37
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; martensitic stainless steel (Table 17)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can BS 970 (Part 3) 416S37 Be Substituted With GOST 5632 06Kh23N28?
BS 970 (Part 3) 416S37 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 3) 416S37
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
BS 970 (Part 3) 416S37
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 416S37 and GOST 5632 06Kh23N28?
BS 970 (Part 3) 416S37 specifies P, S, Mo which are not specified for GOST 5632 06Kh23N28.
Can BS 970 (Part 3) 416S37 be substituted with GOST 5632 06Kh23N28?
BS 970 (Part 3) 416S37 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.