BS 970 (Part 3) 722M24 vs IS 11169 (Part 1) 25Cr13Mo6

Strong Match — 92.1% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 722M24 (BS 970 (Part 3):1991) and IS 11169 (Part 1) 25Cr13Mo6 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 3) 722M24 is typically used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (table 16), while IS 11169 (Part 1) 25Cr13Mo6 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). BS 970 (Part 3) 722M24 is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 25Cr13Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 3) 722M24 vs IS 11169 (Part 1) 25Cr13Mo6 is a 92.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.1%.

Frequently Compared With BS 970 (Part 3) 722M24:
IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr2Mo5V2H IS 1570 (Part 7) 12Cr9Mo10H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 7) 12Cr4Mo5H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5
Match Breakdown
CHEMISTRY MATCH
92.1%
MECHANICAL MATCH
No shared data
OVERALL
92.1%
Specifications
Property BS 970 (Part 3) 722M24 IS 11169 (Part 1) 25Cr13Mo6
Standard BS 970 (Part 3):1991 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.20-0.28 0.20-0.30
Si (%) 0.10-0.40 0.10-0.35
Mn (%) 0.45-0.70 0.40-0.70
P (%) <=0.035 Not specified
S (%) <=0.040 Not specified
Cr (%) 3.00-3.50 2.90-3.40
Mo (%) 0.45-0.65 0.45-0.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 722M24 IS 11169 (Part 1) 25Cr13Mo6
Hardness, annealed Not specified <=190 HB
Typical Applications
BS 970 (Part 3) 722M24
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (Table 16)
IS 11169 (Part 1) 25Cr13Mo6
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can BS 970 (Part 3) 722M24 Be Substituted With IS 11169 (Part 1) 25Cr13Mo6?
BS 970 (Part 3) 722M24 and IS 11169 (Part 1) 25Cr13Mo6 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 25Cr13Mo6 is often considered as a substitute for BS 970 (Part 3) 722M24 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 722M24
0 active listings and RFQs →
IS 11169 (Part 1) 25Cr13Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 722M24 and IS 11169 (Part 1) 25Cr13Mo6?
BS 970 (Part 3) 722M24 specifies P, S which are not specified for IS 11169 (Part 1) 25Cr13Mo6.
Can BS 970 (Part 3) 722M24 be substituted with IS 11169 (Part 1) 25Cr13Mo6?
BS 970 (Part 3) 722M24 and IS 11169 (Part 1) 25Cr13Mo6 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 25Cr13Mo6 is often considered as a substitute for BS 970 (Part 3) 722M24 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.