Minimal Match — 53% match
based on chemical composition and mechanical property overlap.
DIN 17200 28Mn6 (DIN 17200:1986) and BS 970 (Part 1) 045M10 (BS 970 (Part 1):1991) are both steel grades.
Both fall under the Carbon Steel category.
DIN 17200 28Mn6 is typically used for unalloyed manganese carbon steel for quenching and tempering; shafts and machine components requiring good hardenability, moderate strength, while BS 970 (Part 1) 045M10 is commonly used for case hardening steel (section four).
DIN 17200 28Mn6 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while BS 970 (Part 1) 045M10 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, DIN 17200 28Mn6 vs BS 970 (Part 1) 045M10 is a 79.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 53%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
DIN 17200 28Mn6
BS 970 (Part 1) 045M10
Tensile Strength
590-780 MPa
430 MPa min
Yield Strength
390 MPa min
Not specified
Elongation
16% min
18 % min
Hardness
170-223 HB
Not specified
Condition
Not specified
Case hardened, 19 mm test bar
Typical Applications
DIN 17200 28Mn6
Unalloyed manganese carbon steel for quenching and tempering; shafts and machine components requiring good hardenability, moderate strength
BS 970 (Part 1) 045M10
Case hardening steel (section four)
Key Differences
DIN 17200 28Mn6 specifies Si, P, S which are not specified for BS 970 (Part 1) 045M10.
Can DIN 17200 28Mn6 Be Substituted With BS 970 (Part 1) 045M10?
DIN 17200 28Mn6 and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between DIN 17200 28Mn6 and BS 970 (Part 1) 045M10?
DIN 17200 28Mn6 specifies Si, P, S which are not specified for BS 970 (Part 1) 045M10.
Can DIN 17200 28Mn6 be substituted with BS 970 (Part 1) 045M10?
DIN 17200 28Mn6 and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.