DIN 17200 28Mn6 vs BS 970 (Part 1) 080A20

Close Alternative — 79.6% match based on chemical composition and mechanical property overlap.

DIN 17200 28Mn6 (DIN 17200:1986) and BS 970 (Part 1) 080A20 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. DIN 17200 28Mn6 is typically used for unalloyed manganese carbon steel for quenching and tempering; shafts and machine components requiring good hardenability, moderate strength, while BS 970 (Part 1) 080A20 is commonly used for used for nuts, bolts, hydraulic fittings, precision turned parts, sleeves, and couplings.. DIN 17200 28Mn6 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while BS 970 (Part 1) 080A20 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, DIN 17200 28Mn6 vs BS 970 (Part 1) 080A20 is a 79.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79.6%.

Frequently Compared With DIN 17200 28Mn6:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
79.6%
MECHANICAL MATCH
No shared data
OVERALL
79.6%
Specifications
Property DIN 17200 28Mn6 BS 970 (Part 1) 080A20
Standard DIN 17200:1986 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.25-0.32 0.18-0.23
Mn (%) 1.30-1.65 0.70-0.90
Si (%) <=0.40 Not specified
P (%) <=0.040 Not specified
S (%) <=0.040 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17200 28Mn6 BS 970 (Part 1) 080A20
Tensile Strength 590-780 MPa Not specified
Yield Strength 390 MPa min Not specified
Elongation 16% min Not specified
Hardness 170-223 HB Not specified
Typical Applications
DIN 17200 28Mn6
Unalloyed manganese carbon steel for quenching and tempering; shafts and machine components requiring good hardenability, moderate strength
BS 970 (Part 1) 080A20
Used for nuts, bolts, hydraulic fittings, precision turned parts, sleeves, and couplings.
Key Differences
Can DIN 17200 28Mn6 Be Substituted With BS 970 (Part 1) 080A20?
DIN 17200 28Mn6 and BS 970 (Part 1) 080A20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
DIN 17200 28Mn6
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4900–6300 mm (192.91–248.03 in)
BS 970 (Part 1) 080A20
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–6600 mm (188.98–259.84 in)
On M-EX Right Now
DIN 17200 28Mn6
2 active listings and RFQs →
BS 970 (Part 1) 080A20
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17200 28Mn6 and BS 970 (Part 1) 080A20?
DIN 17200 28Mn6 specifies Si, P, S which are not specified for BS 970 (Part 1) 080A20.
Can DIN 17200 28Mn6 be substituted with BS 970 (Part 1) 080A20?
DIN 17200 28Mn6 and BS 970 (Part 1) 080A20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.