Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
DIN 17200 30CrMoV9 (DIN 17200:1986) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
DIN 17200 30CrMoV9 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, DIN 17200 30CrMoV9 vs IS 4367 07Cr4Mo6 is a 54% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
DIN 17200 30CrMoV9
IS 4367 07Cr4Mo6
Tensile Strength
900–1100 MPa
380-550 MPa
Yield Strength
≥750 MPa
225 MPa min
Elongation
≥13%
>=19%
Izod Impact
Not specified
60 J min
Hardness (soft annealed)
Not specified
<=170 HB
Condition
Not specified
Normalised and tempered, ruling section up to 40 mm
Typical Applications
DIN 17200 30CrMoV9
Power generation components, rotors, turbine parts
IS 4367 07Cr4Mo6
Not documented
Key Differences
DIN 17200 30CrMoV9 specifies V which is not specified for IS 4367 07Cr4Mo6.
IS 4367 07Cr4Mo6 specifies Si, Ni, S, P which are not specified for DIN 17200 30CrMoV9.
Can DIN 17200 30CrMoV9 Be Substituted With IS 4367 07Cr4Mo6?
DIN 17200 30CrMoV9 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between DIN 17200 30CrMoV9 and IS 4367 07Cr4Mo6?
DIN 17200 30CrMoV9 specifies V which is not specified for IS 4367 07Cr4Mo6. IS 4367 07Cr4Mo6 specifies Si, Ni, S, P which are not specified for DIN 17200 30CrMoV9.
Can DIN 17200 30CrMoV9 be substituted with IS 4367 07Cr4Mo6?
DIN 17200 30CrMoV9 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.