DIN 17200 30NiCr11 vs GB/T 3077 12Cr2Ni4A

Related Material — 55.6% match based on chemical composition and mechanical property overlap.

DIN 17200 30NiCr11 (DIN 17200:1986) and GB/T 3077 12Cr2Ni4A (GB/T 3077-2015) are both steel grades. Both fall under the Alloy Steel category. DIN 17200 30NiCr11 is typically used for used in heavy-duty gears, crankshafts, aircraft parts, shafts, and connecting rods., while GB/T 3077 12Cr2Ni4A is commonly used for used for gears, shafts, pinions, aircraft parts, heavy-duty bearings, and transmission components.. DIN 17200 30NiCr11 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while GB/T 3077 12Cr2Ni4A is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, DIN 17200 30NiCr11 vs GB/T 3077 12Cr2Ni4A is a 68.7% match. As per mechanical properties, the match is 29.5%. Combined, this makes them a related material overall at 55.6%.

Frequently Compared With DIN 17200 30NiCr11:
UNI 11234 100Cr6 NF A35-565 100C6 GOST 4543 12HN3A IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
68.7%
MECHANICAL MATCH
29.5%
OVERALL
55.6%
Specifications
Property DIN 17200 30NiCr11 GB/T 3077 12Cr2Ni4A
Standard DIN 17200:1986 GB/T 3077-2015
Category Alloy Steel Alloy Steel
C (%) 0.27-0.34 0.10-0.15
Si (%) 0.10-0.40 0.17-0.37
Mn (%) 0.40-0.70 0.30-0.60
Ni (%) 2.50-3.00 3.25-3.75
Cr (%) 0.60-1.00 1.25-1.65
P (%) 0.025 max 0.025 max
S (%) 0.035 max 0.025 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17200 30NiCr11 GB/T 3077 12Cr2Ni4A
Tensile Strength 900-1100 MPa 980-1180 MPa
Yield Strength 700 MPa min 785-980 MPa
Elongation 10-13% 10-14%
Hardness 260-320 HB 58-62 HRC (case)
Typical Applications
DIN 17200 30NiCr11
Used in heavy-duty gears, crankshafts, aircraft parts, shafts, and connecting rods.
GB/T 3077 12Cr2Ni4A
Used for gears, shafts, pinions, aircraft parts, heavy-duty bearings, and transmission components.
Can DIN 17200 30NiCr11 Be Substituted With GB/T 3077 12Cr2Ni4A?
DIN 17200 30NiCr11 and GB/T 3077 12Cr2Ni4A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
DIN 17200 30NiCr11
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6500–6800 mm (255.91–267.72 in)
GB/T 3077 12Cr2Ni4A
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5000–6600 mm (196.85–259.84 in)
On M-EX Right Now
DIN 17200 30NiCr11
2 active listings and RFQs →
GB/T 3077 12Cr2Ni4A
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17200 30NiCr11 and GB/T 3077 12Cr2Ni4A?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can DIN 17200 30NiCr11 be substituted with GB/T 3077 12Cr2Ni4A?
DIN 17200 30NiCr11 and GB/T 3077 12Cr2Ni4A share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.