Post Stock Login Register

DIN 17200 40NiCrMo6 vs IS 4367 07Cr4Mo6

Minimal Match — 40.4% match based on chemical composition and mechanical property overlap.

DIN 17200 40NiCrMo6 (DIN 17200:1986) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. DIN 17200 40NiCrMo6 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, DIN 17200 40NiCrMo6 vs IS 4367 07Cr4Mo6 is a 60.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 40.4%.

Frequently Compared With DIN 17200 40NiCrMo6:
UNI 11234 100Cr6 GOST 4543 12HN3A NF A35-565 100C6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr4 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
60.6%
MECHANICAL MATCH
0%
OVERALL
40.4%
Specifications
Property DIN 17200 40NiCrMo6 IS 4367 07Cr4Mo6
Standard DIN 17200:1986 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.36–0.44 <=0.12
Mn (%) 0.50–0.80 0.40-0.70
Cr (%) 0.60–1.00 0.70-1.10
Mo (%) 0.15–0.30 0.45-0.65
Ni (%) 1.30–1.70 <=0.30
Si (%) Not specified 0.15-0.60
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17200 40NiCrMo6 IS 4367 07Cr4Mo6
Tensile Strength 900–1100 MPa 380-550 MPa
Yield Strength ≥720 MPa 225 MPa min
Elongation ≥12% >=19%
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Condition Not specified Normalised and tempered, ruling section up to 40 mm
Typical Applications
DIN 17200 40NiCrMo6
Heavy forgings, crankshafts, high strength components
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can DIN 17200 40NiCrMo6 Be Substituted With IS 4367 07Cr4Mo6?
DIN 17200 40NiCrMo6 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
DIN 17200 40NiCrMo6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5500–6900 mm (216.54–271.65 in)
IS 4367 07Cr4Mo6
No active listings currently.
On M-EX Right Now
DIN 17200 40NiCrMo6
2 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17200 40NiCrMo6 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies Si, S, P which are not specified for DIN 17200 40NiCrMo6.
Can DIN 17200 40NiCrMo6 be substituted with IS 4367 07Cr4Mo6?
DIN 17200 40NiCrMo6 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.