DIN 17204 36Mn5 vs BS 970 (Part 1) 150M36

Strong Match — 90.4% match based on chemical composition and mechanical property overlap.

DIN 17204 36Mn5 (DIN 17204:1990-11) and BS 970 (Part 1) 150M36 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. DIN 17204 36Mn5 is typically used for unalloyed manganese carbon steel for quenching and tempering, higher manganese content than 28mn6; shafts and machine components requiring higher hardenability and strength, while BS 970 (Part 1) 150M36 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. DIN 17204 36Mn5 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while BS 970 (Part 1) 150M36 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, DIN 17204 36Mn5 vs BS 970 (Part 1) 150M36 is a 90.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.4%.

Frequently Compared With DIN 17204 36Mn5:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
90.4%
MECHANICAL MATCH
No shared data
OVERALL
90.4%
Specifications
Property DIN 17204 36Mn5 BS 970 (Part 1) 150M36
Standard DIN 17204:1990-11 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) 0.32-0.40 0.32-0.40
Mn (%) 1.20-1.50 1.30-1.70
Si (%) <=0.40 Not specified
P (%) <=0.040 <=0.050
S (%) <=0.040 <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17204 36Mn5 BS 970 (Part 1) 150M36
Tensile Strength 650-850 MPa Not specified
Yield Strength 450 MPa min Not specified
Elongation 14% min Not specified
Hardness 187-241 HB Not specified
Typical Applications
DIN 17204 36Mn5
Unalloyed manganese carbon steel for quenching and tempering, higher manganese content than 28Mn6; shafts and machine components requiring higher hardenability and strength
BS 970 (Part 1) 150M36
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can DIN 17204 36Mn5 Be Substituted With BS 970 (Part 1) 150M36?
DIN 17204 36Mn5 and BS 970 (Part 1) 150M36 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 150M36 is often considered as a substitute for DIN 17204 36Mn5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
DIN 17204 36Mn5
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5900–6400 mm (232.28–251.97 in)
BS 970 (Part 1) 150M36
No active listings currently.
On M-EX Right Now
DIN 17204 36Mn5
2 active listings and RFQs →
BS 970 (Part 1) 150M36
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17204 36Mn5 and BS 970 (Part 1) 150M36?
DIN 17204 36Mn5 specifies Si which is not specified for BS 970 (Part 1) 150M36.
Can DIN 17204 36Mn5 be substituted with BS 970 (Part 1) 150M36?
DIN 17204 36Mn5 and BS 970 (Part 1) 150M36 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 150M36 is often considered as a substitute for DIN 17204 36Mn5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.