DIN 17210 18CrNiMo6 vs IS 1570 (Part 4) 20Ni7Cr2Mo2

Related Material — 69.2% match based on chemical composition and mechanical property overlap.

DIN 17210 18CrNiMo6 (DIN 17210:1986) and IS 1570 (Part 4) 20Ni7Cr2Mo2 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. DIN 17210 18CrNiMo6 is defined under Deutsches Institut fur Normung (DIN), originating from Germany, while IS 1570 (Part 4) 20Ni7Cr2Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, DIN 17210 18CrNiMo6 vs IS 1570 (Part 4) 20Ni7Cr2Mo2 is a 69.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.2%.

Frequently Compared With DIN 17210 18CrNiMo6:
GB/T 3077 12Cr2Ni4A NF A35-565 100C6 UNI 11234 100Cr6 GOST 4543 12HN3A IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
69.2%
MECHANICAL MATCH
No shared data
OVERALL
69.2%
Specifications
Property DIN 17210 18CrNiMo6 IS 1570 (Part 4) 20Ni7Cr2Mo2
Standard DIN 17210:1986 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.15–0.21 0.17-0.22
Mn (%) 0.50–0.90 0.45-0.65
Cr (%) 1.50–1.80 0.40-0.60
Ni (%) 1.40–1.70 1.65-2.00
Mo (%) 0.25–0.35 0.20-0.30
Si (%) 0.15–0.40 0.15-0.35
S (%) ≤0.035 Not specified
P (%) ≤0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property DIN 17210 18CrNiMo6 IS 1570 (Part 4) 20Ni7Cr2Mo2
Tensile Strength 1000–1200 MPa Not specified
Case Hardness HRC 58–63 Not specified
Core Hardness HB 280–340 Not specified
Elongation ≥9% Not specified
Typical Applications
DIN 17210 18CrNiMo6
Heavy duty gears, shafts, cams, axles, case hardened transmission components
IS 1570 (Part 4) 20Ni7Cr2Mo2
Not documented
Key Differences
Can DIN 17210 18CrNiMo6 Be Substituted With IS 1570 (Part 4) 20Ni7Cr2Mo2?
DIN 17210 18CrNiMo6 and IS 1570 (Part 4) 20Ni7Cr2Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
DIN 17210 18CrNiMo6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5000–5400 mm (196.85–212.6 in)
IS 1570 (Part 4) 20Ni7Cr2Mo2
No active listings currently.
On M-EX Right Now
DIN 17210 18CrNiMo6
2 active listings and RFQs →
IS 1570 (Part 4) 20Ni7Cr2Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between DIN 17210 18CrNiMo6 and IS 1570 (Part 4) 20Ni7Cr2Mo2?
DIN 17210 18CrNiMo6 specifies S, P which are not specified for IS 1570 (Part 4) 20Ni7Cr2Mo2.
Can DIN 17210 18CrNiMo6 be substituted with IS 1570 (Part 4) 20Ni7Cr2Mo2?
DIN 17210 18CrNiMo6 and IS 1570 (Part 4) 20Ni7Cr2Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.