EN 10025-2 E335 vs AS/NZS 3679.1 350

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10025-2 E335 (EN 10025-2:2019) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 E335 is typically used for hot rolled products of structural steels, while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. EN 10025-2 E335 is defined under European Standard (EN), originating from Europe, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, EN 10025-2 E335 vs AS/NZS 3679.1 350 is a 79.9% match. As per mechanical properties, the match is 10.1%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10025-2 E335:
GOST 19281 09G2S CSA G40.21 260W CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 80 ASTM A572 Gr.65 AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 350W CSA G40.21 400A ASTM A1008 SS Grade 50
Other Structural Steel Grades to Compare With EN 10025-2 E335:
ASTM A283C
Match Breakdown
CHEMISTRY MATCH
79.9%
MECHANICAL MATCH
10.1%
OVERALL
35%
Specifications
Property EN 10025-2 E335 AS/NZS 3679.1 350
Standard EN 10025-2:2019 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
P (%) <=0.045 <=0.040
S (%) <=0.045 <=0.040
N (%) <=0.012 Not specified
C (%) Not specified <=0.22
Mn (%) Not specified <=1.70
Si (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 E335 AS/NZS 3679.1 350
Tensile Strength 570-710 MPa 480-640 MPa
Yield Strength >=335 MPa 350 MPa min
Elongation >=16% 20% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 E335
Hot rolled products of structural steels
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Key Differences
Can EN 10025-2 E335 Be Substituted With AS/NZS 3679.1 350?
EN 10025-2 E335 and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 E335
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
EN 10025-2 E335
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 E335 and AS/NZS 3679.1 350?
EN 10025-2 E335 specifies N which is not specified for AS/NZS 3679.1 350. AS/NZS 3679.1 350 specifies C, Mn, Si which are not specified for EN 10025-2 E335.
Can EN 10025-2 E335 be substituted with AS/NZS 3679.1 350?
EN 10025-2 E335 and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.