EN 10025-2 S275J2 vs EN 10025-2 S275J0

Strong Match — 97.9% match based on chemical composition and mechanical property overlap.

EN 10025-2 S275J2 (EN 10025-2:2019) and EN 10025-2 S275J0 (EN 10025-2:2019) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S275J2 is typically used for hot rolled products of structural steels, while EN 10025-2 S275J0 is commonly used for hot rolled products of structural steels. EN 10025-2 S275J2 is defined under European Standard (EN), originating from Europe, while EN 10025-2 S275J0 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10025-2 S275J2 vs EN 10025-2 S275J0 is a 96.9% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 97.9%.

Other Structural Steel Grades to Compare With EN 10025-2 S275J2:
GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A283C
Match Breakdown
CHEMISTRY MATCH
96.9%
MECHANICAL MATCH
100%
OVERALL
97.9%
Specifications
Property EN 10025-2 S275J2 EN 10025-2 S275J0
Standard EN 10025-2:2019 EN 10025-2:2019
Category Structural Steel Structural Steel
C (%) <=0.21 <=0.21
Mn (%) <=1.50 <=1.50
P (%) <=0.025 <=0.030
S (%) <=0.025 <=0.030
Cu (%) <=0.55 <=0.55
N (%) Not specified <=0.012
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S275J2 EN 10025-2 S275J0
Tensile Strength 410-560 MPa 410-560 MPa
Yield Strength >=275 MPa >=275 MPa
Elongation >=23% >=23%
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Applications
EN 10025-2 S275J2
Hot rolled products of structural steels
EN 10025-2 S275J0
Hot rolled products of structural steels
Key Differences
Can EN 10025-2 S275J2 Be Substituted With EN 10025-2 S275J0?
EN 10025-2 S275J2 and EN 10025-2 S275J0 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S275J0 is often considered as a substitute for EN 10025-2 S275J2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10025-2 S275J2
0 active listings and RFQs →
EN 10025-2 S275J0
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S275J2 and EN 10025-2 S275J0?
EN 10025-2 S275J0 specifies N which is not specified for EN 10025-2 S275J2.
Can EN 10025-2 S275J2 be substituted with EN 10025-2 S275J0?
EN 10025-2 S275J2 and EN 10025-2 S275J0 overlap closely enough on chemistry and mechanical properties that EN 10025-2 S275J0 is often considered as a substitute for EN 10025-2 S275J2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.