EN 10025-2 S460K2 vs AS/NZS 3679.1 350

Related Material — 64% match based on chemical composition and mechanical property overlap.

EN 10025-2 S460K2 (EN 10025-2:2019) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S460K2 is typically used for hot rolled products of structural steels, while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. EN 10025-2 S460K2 is defined under European Standard (EN), originating from Europe, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, EN 10025-2 S460K2 vs AS/NZS 3679.1 350 is a 89.7% match. As per mechanical properties, the match is 12.5%. Combined, this makes them a related material overall at 64%.

Frequently Compared With EN 10025-2 S460K2:
CSA G40.21 260W CSA G40.21 300W CSA G40.21 350W CSA G40.21 400A CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A283C
Other Structural Steel Grades to Compare With EN 10025-2 S460K2:
GOST 19281 09G2S AS/NZS 3679.1 300 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
89.7%
MECHANICAL MATCH
12.5%
OVERALL
64%
Specifications
Property EN 10025-2 S460K2 AS/NZS 3679.1 350
Standard EN 10025-2:2019 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.22
Si (%) <=0.55 <=0.50
Mn (%) <=1.70 <=1.70
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.040
N (%) <=0.025 Not specified
Cu (%) <=0.55 Not specified
Nb (%) <=0.05 Not specified
V (%) <=0.13 Not specified
Ti (%) <=0.05 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S460K2 AS/NZS 3679.1 350
Tensile Strength 550-720 MPa 480-640 MPa
Yield Strength >=460 MPa 350 MPa min
Elongation >=17% 20% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S460K2
Hot rolled products of structural steels
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Key Differences
Can EN 10025-2 S460K2 Be Substituted With AS/NZS 3679.1 350?
EN 10025-2 S460K2 and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 S460K2
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
EN 10025-2 S460K2
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S460K2 and AS/NZS 3679.1 350?
EN 10025-2 S460K2 specifies N, Cu, Nb, V which are not specified for AS/NZS 3679.1 350.
Can EN 10025-2 S460K2 be substituted with AS/NZS 3679.1 350?
EN 10025-2 S460K2 and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.